Název: Influence of severe plastic deformation and subsequent annealing on creep behaviour of martensitic 9% Cr steel
Autoři: Král, Petr ; Dvořák, Jiří ; Sklenička, Václav ; Horita, Z. ; Tokizawa, Y. ; Tang, Y. ; Kunčická, Lenka ; Kuchařová, Květa ; Kvapilová, Marie ; Svobodová, M.
Typ dokumentu: Příspěvky z konference
Konference/Akce: Metal 2021 - International Conference on Metallurgy and Materials /30./, Brno (CZ), 20210526
Rok: 2021
Jazyk: eng
Abstrakt: The objective of the study is to evaluate the effects of severe plastic deformation (SPD) and annealing on creep behaviour of advanced tungsten modified creep-resistant 9 % Cr martensitic P92 steel. The as-received P92 steel was deformed by high-pressure torsion (HTP), high-pressure sliding (HPS) and rotary swaging (RS) at room temperature prior creep testing. These SPD methods imposed significantly different equivalent plastic strain in the range from 1 up to 20. Constant load creep tests in tension were performed in an argon atmosphere at 873 K and applied stress ranging from 50 to 200 MPa. The microstructure and phase composition of P92 steel were studied using a scanning electron microscope Tescan Lyra 3 and a transmission electron microscope Jeol 2100F. The results show that under the same creep loading conditions the HPT and HPS-processed P92 steel exhibited significantly faster minimum creep rates, creep fracture strain and the decrease in the value of the stress exponent of the creep rate in comparison with as-received P92 steel. However, it was revealed that the RS-processed specimens exhibited one order of magnitude lower minimum creep rate and lower ductility compared to commercial P92 steel. The creep curves for the HPT and HPS-processed states exhibited a pronounced minimum of strain rate. The pronounced minimum of strain rate disappeared when these states were annealed at 923K/500h before application of creep loading. The microstructure changes occurring during creep and different creep behaviour between as-received and deformed states are discussed.
Klíčová slova: creep; Creep-resistant 9 %Cr steels; microstructure; severe plastic deformation
Číslo projektu: GA19-18725S (CEP)
Poskytovatel projektu: GA ČR
Zdrojový dokument: METAL 2021. 30th Anniversary International Conference on Metallurgy and Materials. Conference proceedings, ISBN 978-80-87294-99-4, ISSN 2694-9296

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: https://hdl.handle.net/11104/0345965

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-534643


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference
 Záznam vytvořen dne 2023-10-16, naposledy upraven 2023-10-17.


Není přiložen dokument
  • Exportovat ve formátu DC, NUŠL, RIS
  • Sdílet