Název: INFLUENCE OF ECAP TECHNIQUE ON CREEP BEHAVIOUR OF POWDER ALUMINIUM PROCESSED BY DIRECT EXTRUSION
Autoři: Dvořák, Jiří ; Král, Petr ; Balog, M. ; Simančík, F. ; Sklenička, Václav
Typ dokumentu: Příspěvky z konference
Konference/Akce: NANOCON 2010. International Conference /2./, Olomouc (CZ), 2010-10-12 / 2010-10-14
Rok: 2010
Jazyk: eng
Abstrakt: The Al powder was prepared by cold isostatic pressing at the pressure of 200 MPa. The granulometric powder fraction of a particle size less than 400 µm was compacted via conventional direct hot-extrusion (DE) at temperature 450°C. This material was then subjected to ECAP technique up to 4 passes. The microstructural investigations were performed using OM and SEM equipped with an EBSD unit. Creep tests in tension were conducted at temperature of 473 K and at applied stresses in the range from 30 to 60 MPa. Some creep tests in compression were performed on material just after DE. The paper presents results of study of microstructure and creep behaviour of aluminium powder before and after ECAP. It was found that ECAP method does not lead to an additional marked refinement of grain size. However, in dependence on number of ECAP passes ECAP method markedly influences creep behaviour due to development of high-angle grain boundaries during ECAP process.
Klíčová slova: CREEP; ECAP; powder aluminium; ultrafine-grained material
Číslo projektu: CEZ:AV0Z20410507 (CEP), KJB200410801 (CEP)
Poskytovatel projektu: GA AV ČR
Zdrojový dokument: Nanocon 2010, ISBN 978-80-87294-18-5

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0191225

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-42132


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference