| Home > Conference materials > Papers > INFLUENCE OF ECAP TECHNIQUE ON CREEP BEHAVIOUR OF POWDER ALUMINIUM PROCESSED BY DIRECT EXTRUSION |
Original title:
INFLUENCE OF ECAP TECHNIQUE ON CREEP BEHAVIOUR OF POWDER ALUMINIUM PROCESSED BY DIRECT EXTRUSION
Authors: Dvořák, Jiří ; Král, Petr ; Balog, M. ; Simančík, F. ; Sklenička, Václav
Document type: Papers
Conference/Event: NANOCON 2010. International Conference /2./, Olomouc (CZ), 2010-10-12 / 2010-10-14
Year: 2010
Language: eng
Abstract: The Al powder was prepared by cold isostatic pressing at the pressure of 200 MPa. The granulometric powder fraction of a particle size less than 400 µm was compacted via conventional direct hot-extrusion (DE) at temperature 450°C. This material was then subjected to ECAP technique up to 4 passes. The microstructural investigations were performed using OM and SEM equipped with an EBSD unit. Creep tests in tension were conducted at temperature of 473 K and at applied stresses in the range from 30 to 60 MPa. Some creep tests in compression were performed on material just after DE. The paper presents results of study of microstructure and creep behaviour of aluminium powder before and after ECAP. It was found that ECAP method does not lead to an additional marked refinement of grain size. However, in dependence on number of ECAP passes ECAP method markedly influences creep behaviour due to development of high-angle grain boundaries during ECAP process.
Keywords: CREEP; ECAP; powder aluminium; ultrafine-grained material
Project no.: CEZ:AV0Z20410507 (CEP), KJB200410801 (CEP)
Funding provider: GA AV ČR
Host item entry: Nanocon 2010, ISBN 978-80-87294-18-5
Institution: Institute of Physics of Materials AS ČR (web)
Document availability information: Fulltext is available at the institute of the Academy of Sciences.
Original record: http://hdl.handle.net/11104/0191225
Permalink: http://www.nusl.cz/ntk/nusl-42132
The record appears in these collections:
Research > Institutes ASCR > Institute of Physics of Materials
Conference materials > Papers
Authors: Dvořák, Jiří ; Král, Petr ; Balog, M. ; Simančík, F. ; Sklenička, Václav
Document type: Papers
Conference/Event: NANOCON 2010. International Conference /2./, Olomouc (CZ), 2010-10-12 / 2010-10-14
Year: 2010
Language: eng
Abstract: The Al powder was prepared by cold isostatic pressing at the pressure of 200 MPa. The granulometric powder fraction of a particle size less than 400 µm was compacted via conventional direct hot-extrusion (DE) at temperature 450°C. This material was then subjected to ECAP technique up to 4 passes. The microstructural investigations were performed using OM and SEM equipped with an EBSD unit. Creep tests in tension were conducted at temperature of 473 K and at applied stresses in the range from 30 to 60 MPa. Some creep tests in compression were performed on material just after DE. The paper presents results of study of microstructure and creep behaviour of aluminium powder before and after ECAP. It was found that ECAP method does not lead to an additional marked refinement of grain size. However, in dependence on number of ECAP passes ECAP method markedly influences creep behaviour due to development of high-angle grain boundaries during ECAP process.
Keywords: CREEP; ECAP; powder aluminium; ultrafine-grained material
Project no.: CEZ:AV0Z20410507 (CEP), KJB200410801 (CEP)
Funding provider: GA AV ČR
Host item entry: Nanocon 2010, ISBN 978-80-87294-18-5
Institution: Institute of Physics of Materials AS ČR (web)
Document availability information: Fulltext is available at the institute of the Academy of Sciences.
Original record: http://hdl.handle.net/11104/0191225
Permalink: http://www.nusl.cz/ntk/nusl-42132
The record appears in these collections:
Research > Institutes ASCR > Institute of Physics of Materials
Conference materials > Papers
Record created 2011-07-04, last modified 2024-01-26