Prediction of static materials properties of P92 steel based on small punch test
Dymáček, Petr ; Ječmínka, M. ; Abendroth, M.
Small punch testing under constant deflection rate of P92 steel at room temperature was performed. The experimental SPT curves were used for prediction of yield and ultimate strength based on empirical formulas published in the literature and also by numerical inverse analysis with help of finite element method. Conventional tensile tests were performed for verification of the data derived from small punch testing. Good agreement was found in the case of ultimate strength. Determination of the yield strength is less accurate mainly due to significantly lower values of force at yield compared to maximum force measured by SPT. Two approaches for evaluation and determination of the force at yield limit in SPT diagram and estimation of the yield strength of the material are described in the article.
|
| |
|
Deskripce zubní úrazovosti u chlapců staršího školního věku v mikroregionu České Budějovice a návrh zdravotně edukačního materiálu.
TOBOLKOVÁ, Andrea
Diplomová práce se zabývá problematikou zubní úrazovosti u chlapců staršího školního věku v mikroregionu České Budějovice. Úraz znamená náhlé poškození zdraví působením vnějších faktorů o síle přesahující adaptační možnosti lidského organismu. V oblasti zubní úrazovosti jsou nejvíce ohroženou skupinou populace děti. Nejčastějším důvodem úrazu malých dětí je jejich nedokonalá stabilita. V případě starších dětí a mládeže převažují úrazy vzniklé vlivem sportu. Teoretická část diplomové práce je zaměřena na vymezení období staršího školního věku, dále pak na anatomii a fyziologii chrupu. Součástí práce je i výčet zubních úrazů a jejich následná léčba. Pozornost také patří protetické stomatologii a vlivu úrazů na fyzické a psychické zdraví jedince. V závěru teoretické části je uveden postup při vyšetření zraněného, poúrazová dentální hygiena a výživa pacienta po úrazu zubů. Výzkumná část práce zjišťuje pomocí dotazníkového šetření druhy úrazů zubů, okolnosti vzniku úrazů a vliv úrazů na fyzické a psychické zdraví jedinců dané věkové kategorie. Dotazníkové šetření bylo vyhodnoceno a následně zpracováno v grafické části práce. Součástí diplomové práce je i zdravotně edukační materiál, který slouží ke zkvalitnění dentální hygieny a k prevenci vzniku zubních úrazů u žáků 2. stupně základní školy.
|
|
Drobní savci v potravě sovy pálené ve východním Středomoří.
Šindelář, Jiří ; Horáček, Ivan (vedoucí práce) ; Anděra, Miloš (oponent)
Obsáhlý materiál kosterních pozůstatků savců z potravy sovy pálené v oblasti východního Středomoří byl zpracován a různými technikami chorologické a morfometrické analýzy zhodnocen. Ve vlastním souboru, obsahujícím doklady nejméně 8400 jedinců, je zastoupeno celkem 45 druhů hmyzožravců, hlodavců a netopýrů, kteří reprezentují podstatnou část fauny regionu. Podrobně byla zhodnocena chorologická skladba tafocenos a meziregionální rozdíly, projevující se především odlišnostmi v zastoupení satelitních a akcesorických elementů. Vysoce průkazné je ochuzení tafocenos izolovaných ostrovů (Kypr, Karpathos, zčásti Kréta), kde chybí křečkovití, hrabošovití, C. leucodon aj. a v dominanční struktuře se zásadním dílem uplatňuje krysa Rattus rattus, představující zde invazní druh, výrazně úspěšnější než v členitých kontinentálních kontextech. Druhová diverzita zkoumaných tafocenos je pozitivně korelována s geografickou šířkou (tafocenosy severnějších regionů jsou výrazně bohatší) a negativně s ostrovním efektem a stupněm aridizace. Morfometrická analýza tří nejhojnějších druhů rejskovitých ukázala z hlediska zkoumaného regionu výrazně homogenní distribuci metrických charakteristik jednotlivých druhů, v lokálním měřítku se však tato homogenita u některých druhů ztrácí. U C. leucodon je patrný aspekt klinální...
|
| |
| |
|
HYDROGENATION PROPERTIES OF BALL-MILLED Mg-Ti-C-Zr COMPOSITE
Král, Lubomír ; Čermák, Jiří ; Roupcová, Pavla
The hydrogen storage properties of ball-milled Mg-Ti-Zr-C composite (1.8 wt.% Ti, 1.9 wt.% Zr and 0.2 wt.% C) were investigated. It has been previously shown, that the addition of Ti, Zr and C improved its storage properties. This beneficial effect of additives upon hydrogen storage properties can be explained by catalysis by the particles rich in Ti or Zr located on the surface of Mg grains. They provide effective pathways for the hydrogen diffusion into the MgH2. The morphological and microstructural characteristics were investigated by scanning electron microscopy and by X-ray diffraction. The hydrogen sorption was measured by Sieverts method using Setaram PCT-Pro device. In this paper, sorption behaviour of the composite after ball-milling and after aging on the air was compared. The ball-milled composite adsorbed 3.5 wt.% H2 within 10 min at 623 K. However, hydrogen storage capacity of the composite aged on the air for 7 months remarkably decreased: The aged composite adsorbed within 10 min only 2 wt.% H2 at 623 K and the sorption capacity decreased from 4.7 wt.% H2 to 2.1 wt.% H2.
|
|
INFLUENCE OF LASER CUTTING AND PUNCHING ON MAGNETIC PROPERTIES\nOF ELECTRICAL STEEL M470-50A
Bulín, Tomáš ; Švábenská, Eva ; Hapla, Miroslav ; Ondrůšek, Č. ; Schneeweiss, Oldřich
Electrical steel M470-50A belongs to the most often used materials in electrical machines. Due to this fact, it is desirable to know the magnetic parameters after processing raw sheets into the required shape. Basic parameters of mechanical, electrical, and magnetic properties of the sheets are usually obtained from the producer but the magnetic properties are changing in dependence on additional machining processes. The aim of this study is to describe changes in parameters of magnetic behavior after punching, laser and spark cutting of the original sheets. The basic information of structure was obtained by optical and scanning electron microscopy. The magnetic parameters were acquired from the measuring of magnetic hysteresis loops in dependence on saturation fields and frequencies. The results are discussed from the point of view of applied\ncutting technology with the aim to obtain the best magnetic parameters and consequently a higher efficiency of the final product. Results can be used as input parameters in simulation of the electrical machine.
|
|
Changes in structure and phase composition in the surface of tram rail
Švábenská, Eva ; Roupcová, Pavla ; Schneeweiss, Oldřich
We have investigated structure and phase composition of surface layer of tram rails after long time running and the results were compared with those obtained on the original part of material. Changes due to effects of severe plastic deformation together with thermal shocks by friction process were expected. The information about structure and phase composition was obtained by optical and scanning electron microscopy, X-Ray Powder Diffraction, Mössbauer Spectroscopy and Glow Discharge Emission Spectroscopy (GDOES) and this was completed by microhardness measurements. The results show that the surface layer in comparison with the original material exhibits important changes in grain structure, an increase in microhardness and high content of iron oxide and hydrooxides. According to the depth profile of the chemical composition measured by GDOES there is an increase in carbon content in the surface layer which can be effect of up-hill diffusion.
|
|
STRAIN ENGINEERING OF THE ELECTRONIC STRUCTURE OF 2D MATERIALS
del Corro, Elena ; Peňa-Alvarez, M. ; Morales-García, A. ; Bouša, Milan ; Řáhová, Jaroslava ; Kavan, Ladislav ; Kalbáč, Martin ; Frank, Otakar
The research on graphene has attracted much attention since its first successful preparation in 2004. It possesses many unique properties, such as an extreme stiffness and strength, high electron mobility, ballistic transport even at room temperature, superior thermal conductivity and many others. The affection for graphene was followed swiftly by a keen interest in other two dimensional materials like transition metal dichalcogenides. As has been predicted and in part proven experimentally, the electronic properties of these materials can be modified by various means. The most common ones include covalent or non-covalent chemistry, electrochemical, gate or atomic doping, or quantum confinement. None of these methods has proven universal enough in terms of the devices' characteristics or scalability. However, another approach is known mechanical strain/stress, but experiments in that direction are scarce, in spite of their high promises.\nThe primary challenge consists in the understanding of the mechanical properties of 2D materials and in the ability to quantify the lattice deformation. Several techniques can be then used to apply strain to the specimens and thus to induce changes in their electronic structure. We will review their basic concepts and some of the examples so far documented experimentally and/or theoretically.
|
host ::