Influence of Microstructure Instability on Creep Behaviour of UFG Pure Materials
Král, Petr ; Dvořák, Jiří ; Svoboda, Milan ; Kvapilová, Marie ; Sklenička, Václav
Experiments were conducted to determine an effect of creep temperature on creep behaviour of pure Cu. The ECAP pressing was performed at room temperature by route Bc. Constant load creep tests in tension were conducted at 373-573 K under different stresses. The values of the stress exponent n of the minimum creep rate for ultrafine-grained (UFG) and coarse-grained material were determined. Microstructure of samples was characterized by transmission electron microscope (TEM) and scanning electron microscope (SEM) equipped with the electron backscatter unit (EBSD). The microstructure analyses showed that microstructure of pure Cu processed by 8 ECAP passes and subsequent creep exposure contained large fraction of boundaries with coincidence sites lattice (CSL). The results showed that creep in UFG materials is influenced by additional creep mechanisms up to 0.5 Tm when the UFG microstructure in more or less stable.
|
|
| |
|
|
Orientation of Grains in the Al-Mg-Si-Mn Alloy by Scanning Low Energy Electron Microscopy
Müllerová, Ilona ; Matsuda, K. ; Horiba, K. ; Mikmeková, Šárka ; Frank, Luděk
Electron Backscatter Diffraction (EBSD) is a technique allowing the crystallographic infomiation to be obtained from samples in the scanning electron microscope (SEM). The main disadvantages of this method include the specimen tilt by 70°, requiring to operate at large working distances and hence with reduced lateral resolution, and a long acquisition time needed to obtain the full infomnation about grain orientations. However, the crystal orientation can be recognized upon energy dependence of the electron reflectance in the very low energy range. Information can be acquired at a high lateral resolution, high contrast and short acquisition time in a dedicated SEM equipped by the cathode lens.
|
|
| |
|
| |
|
| |
|
| |
|
|
Vliv mikrostrukturních změn na mechanické chování hliníku připraveného extrémní plastickou deformací (ECAP)
Král, Petr ; Dvořák, Jiří ; Svoboda, Milan ; Sklenička, Václav
Extrémně hrubozrnný hliník (99,99%) byl podroben intenzivní plastické deformaci metodou ECAP při pokojové teplotě. Vlastnosti ECAP materiálu mohou být významně odlišné od vlastnostímateriálů se standardní velikostí zrna. Největší změny mikrostruktury probíhají během prvních 4 průchodů. Mikrostruktura po 12 průchodech obsahuje přibližněrovnoosá zrna (~1m) s vysokým množstvím velkoúhlových hranic zrn (~70%). V práci je blíže studováno chování ECAP materiálu s různým počtem průchodů při creepovém a mechanickém tahovém zatěžování. Mechanické zkoušky ukazují, že ECAP hliník vykazuje významné zvýšení pevnostních vlastností (Rm, Rp0,2), ale také nízké deformační zpevnění během zatěžování. Creepová životnost hliníku významně vzrůstá po 1 ECAP průchodu. Avšak, další zvyšování počtu ECAP průchodů vede k poklesu creepových vlastností. ECAP mikrostruktura byla analyzována z hlediska její nehomogenity. Výsledky ukazují, že nehomogenita ECAP mikrostruktury může mít vliv na creepové chování ECAP materiálu.
|