High speed drilling of aluminium plates
Pilný, Lukáš ; Humár, Anton (oponent) ; Píška, Miroslav (vedoucí práce)
Optimization of the metal drilling process requires creation of minimum amount of burrs and uniform appearance of the drilled holes. The goal was to understand the role of various key factors such as cutting conditions, clamping conditions and drill geometry on burr formation when 2 mm sheets of wrought aluminium alloy Al99.7Mg0.5Cu-H24, using 1.6 and 2 mm diameter drills, so that the burr formation could be minimized and an uniform hole surface obtained for a great number of holes drilled on a single workpiece. This goal was approached by three subsequent investigations. First, an experimental test was performed to investigate the effect of cutting speed and feed per revolution, as the most recognized drilling parameters influencing burr formation, on the resulting burr size and drilled hole uniformity. Second, a vacuum clamping system, used to hold the aluminium sheet and restrict the space for burr formation at the drill exit, was constructed and tested for its influence on burr formation. Third, the effect of different drill geometries on burr formation and the uniformity of hole appearance was evaluated. Results from the first experiment showed that burr height and width is reduced at both the entry and exit sides of a sheet when a higher cutting speed is used. With greater feed rates, it was found that burr height and width increase on both sides, with the exception of the height of burrs on the entry side, which may be minimally decreased. The second experiment showed that a properly designed vacuum clamp fixture can be used to significantly reduce exit-side burr formation. In the third experiment, a three flute drill with a properly constructed vacuum clamp was found to eliminate both entry and exit burrs, the demand on the uniform appearance of drilled holes was fulfilled as well as high productivity achieved. Such optimized process requiring no additional deburring results in a noticeable production cost reduction. Furthermore, recommendations for further research into improvements of the production process are made.
|
|
Studium radiačního poškození nádoby reaktoru VVER-440 jaderné elektrárny Dukovany
Říha, Tomáš ; Martinec, Jiří (oponent) ; Šen, Hugo (vedoucí práce)
Diplomová práce se zabývá radiačním poškozením reaktorových nádob jaderných reaktorů, konkrétně pak poškozením TNR 3. bloku jaderné elektrárny Dukovany. V obecné rovině práce popisuje mechanismy poškození reaktorových ocelí a formou rešerše uvádí možnosti sledování stavu materiálu a regenerace materiálových vlastností na jaderných elektrárnách po celém světě. Praktická část je zaměřena na interpretaci výsledků analýz provedených pomocí kódu MOBY-DICK. Jádrem těchto analýz je vývoj fluence neutronů na různých místech reaktorové nádoby od počátku provozu až dodnes, tedy do 24. kampaně. Tyto výsledky jsou diskutovány s ohledem na provedené provozní kontroly. Na tuto část navazují výpočty fluence neutronů pro budoucí palivové vsázky až do 34. kampaně pro vybrané typy paliv. Výsledkem praktické části je srovnání vlivu těchto typů paliv na radiační poškození TNR.
|
| |
| |
|
EXPERIMENTAL STUDY OF PIB-BASED CVD GRAPHENE TRANSFER EFFICIENCY
Bouša, Milan ; Kalbáč, Martin ; Jirka, Ivan ; Kavan, Ladislav ; Frank, Otakar
The transfer of graphene prepared by Chemical Vapor Deposition (CVD) from metal catalyst to target substrate is an important step in preparing desirable nanoscale structures in various fields of science, and thus searching for fast, cheap and clean method attracts great interest. Investigation of mechanical properties of graphene, which are crucial for applications in flexible electronics, performed on bendable synthetic materials, requires a transfer technique using polymers soluble in aliphatic solvents harmless for target polymer substrates. In this study we explore a dry technique using polydimethylsiloxane (PDMS) as stamping polymer and polyisobutylene (PIB) layer as graphene-support polymer. After the transfer PDMS is peeled off and PIB is dissolved in hexane, hence this method fulfils the above mentioned prerequisite. The effectiveness of this transfer was examined by scanning electron microscopy, optical microscopy and Raman microspectroscopy including micro-mapping, and finally by X-ray photoelectron spectroscopy. With all methods carried out, it was found that this sort of stamp-technique is suitable for a high precision transfer of small grains of CVD graphene onto polymer substrates with large yields and similar purity compared to poly(methylmethacrylate) (PMMA)based transfer methods. However, it introduces substantial quantity of surface discontinuities, and therefore this is not a proper method for large scale applications.
|
|
Vliv metody ECAP na mikrostrukturu a creepové chování slitiny AL-3Mg-0,2Sc
Dvořák, Jiří ; Král, Petr ; Kvapilová, Marie ; Sklenička, Václav
Na slitině Al-3Mg-0,2Sc byl zkoumán vliv metody ECAP na její creepové chování a mikrostrukturu.Hrubozrnný materiál o počáteční velikosti zrna ~ 0,5 mm byltvářen metodou ECAP při pokojové teplotě.Creepové testy v tlaku byly provedeny na obou stavech materiálu při aplikaci napětí v rozsahu 16-80 MPa a teplotě 473 K. Výsledky ukázaly, že hodnota minimální creepové rychlosti ultrajemnozrnného materiálu je asi o 2 řády vyšší v porovnání s jeho hrubozrnnou verzí.Mikrostrukturní analýza (TEM, EBSD) prokázala redukci zrna po ECAP na ~ 300nm a zároveň vyšší výskyt velkoúhlových hranic v porovnání s hrubozrnným stavem. Je třeba zdůraznit, že aplikací osmi ECAP průchodů dochází k výraznému snížení creepové odolnosti této slitiny.Na základě výsledků je možné předpokládat, že creepové chování ultrajemnozrné slitiny Al-3Mg-0,2Scje řízeno pokluzy po hranicích zrn akodomovaných difúzí kontrolovaným pohybem mobilních dislokací uvnitř zrn.
|
| |
| |
|
Signalizace protein kinázy B a exprese cyklooxygenáz v časných fázích diabetické nefropatie
Ždychová, Jana ; Komers, Radko (vedoucí práce) ; Haluzík, Martin (oponent) ; Matoušovic, Karel (oponent) ; Škrha, Jan (oponent)
Akt kináza (Akt) je součástí kaskád převádějících signály vasoaktivních a růstových faktorů. Akt- dependentní procesy se podílejí na regulaci mechanismů relevantních pro renální patofyziologii jako jsou syntéza proteinů, viabilita, produkce NO, reabsorbce sodíku atd. Poruchy regulace renálních isoforem cyklooxygenáz produkujících biologicky významné prostanoidy mohou rovněž přispět k známým patofyziologickým mechanismům v rozvoji nefropatie a hypertenze jako důsledek molekulárních abnormalit při diabetu. Cíl: Práce je zaměřena na studium aktivity Akt a jejích efektorů, proteinů "mammalian target of rapamycin"(mTOR) a endoteliální NO syntázy (eNOS), spolu s expresí a aktivitou cyklooxygenázy 2 (COX2) v časných fázích diabetu a jejich úlohu v patofyziologii renálních moďologických a hemodynamických změn při diabetu. Materiál a metody: Aktivita Akt v renálním kortexu byla měřena pomocí kinázové assay. Exprese proteinů byla kvantifikována immunoblottingem. Studie byly prováděny na modelu DMI, tj. na potkanech u nichž byl diabetes navozen podáním streptozotocinu. Pokusná zviřata byla rozdělena do 3 skupin. První skupina diabetických zvířat byla ponechána bez léčby (STZO), druhá skupina (STZ4) byla léčena 4 jednotkanň insulinu denně a třetí skupina (STZ 12) byla léčena 12 jednotkanů insulinu denně. Cílem...
|
host ::