Název: Microstructure, tensile properties and fatigue behaviour of bulk nanoquasicrystalline Al alloy Al93Fe3Cr2Ti2
Autoři: Chlupová, Alice ; Chlup, Zdeněk ; Kruml, Tomáš ; Kuběna, Ivo ; Roupcová, Pavla
Typ dokumentu: Příspěvky z konference
Konference/Akce: NANOCON 2011. International Conference /3./, Brno (CZ), 2011-09-21 / 2011-09-23
Rok: 2011
Jazyk: eng
Abstrakt: The characterization of mechanical properties (i.e. stress-strain characteristics measured in tensile and fatigue tests) together with description of the microstructure of bulk nanocrystalline Al alloy is reported. Aluminium based material used in this work was prepared by hot extrusion of gas atomised powder of chemical composition Al93Fe3Cr2Ti2 which contains nanosized quasicrystalline phase. Changes in fracture mechanisms both at fatigue testing performed at room temperature and at tensile tests performed at different test temperatures were investigated. The quality of powder compaction after extrusion was proved as sufficient. Strong texture in longitudinal direction resulting from production route was detected. Presence of icosahedral phase in material was confirmed by TEM and XRD techniques. Fractographical analysis of fracture surface was performed and results were used for description of fracture mechanisms.
Klíčová slova: Al alloy; fatigue; nanostructured materials; quasicrystals
Číslo projektu: CEZ:AV0Z20410507 (CEP), GAP204/11/1453 (CEP)
Poskytovatel projektu: GA ČR
Zdrojový dokument: NANOCON 2011. Conference Proceedings, ISBN 978-80-87294-23-9

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0203954

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-81442


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference