Název: Creep Behaviour and Microstructure of Ultrafine Grained Iron Processed by ECAP
Autoři: Král, Petr ; Dvořák, Jiří ; Kvapilová, Marie ; Svoboda, Milan ; Sklenička, Václav
Typ dokumentu: Příspěvky z konference
Konference/Akce: Nanocon 2011, Brno (CZ), 2011-09-21 / 2011-09-23
Rok: 2011
Jazyk: eng
Abstrakt: Pure iron (99.99%) was subjected to equal-channel angular pressing (ECAP) with a die having an internal channel of 90°. The subsequent extrusion passes were performed by route A up to 4 passes. The microstructures of UFG iron were investigated using EBSD (electron back scatter diffraction) and transmission el. microscopy (TEM). Tension creep tests were performed on the as-pressed samples at temperature of 773 K and under applied load 60 MPa. For comparison purposes the same creep test was performed also on the unpressed state. The effect of number ECAP passes on creep behavior of pure Fe was investigated. Results showed that the creep resistance of pure Fe after ECAP is improved in comparison with the unpressed state.
Klíčová slova: creep behaviour; equal-channel angular pressing; ultrafine-grained materials
Číslo projektu: CEZ:AV0Z20410507 (CEP), GPP108/10/P469 (CEP)
Poskytovatel projektu: GA ČR
Zdrojový dokument: NANOCON 2011. Conference Proceedings, ISBN 978-80-87294-23-9

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0201832

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-80772


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference