Název:
The Effect of Potassium Oxide K2O on the Purity of C3A
Autoři: Jančíková, Andrea ; Ravaszová, Simona ; Dvořák, Karel ; Křištof, Michal
Typ dokumentu: Příspěvky z konference
Jazyk: eng
Nakladatel: Vysoké učení technické v Brně,Fakulta stavební
Abstrakt: The article is devoted to the study of the preparation and stabilization of pure cubic phase of tricalcium aluminate C₃A. The findings from the literature and several experimental trials have been summarized. Based on these findings, the synthesis of C₃A was realized, and high purity of this mineral was achieved. Furthermore, the influence of foreign ions, mainly in the form of potassium oxide K₂O combined with Na₂O in the form of sodium oxide on the crystal structure was investigated. The transformation of the cubic phase of C₃A into an orthorhombic phase was observed when the amount of these ions in the structure was changed.
Klíčová slova: C3A; clinker; crystal structure; high purity; Potassium oxide; tricalcium aluminate
Zdrojový dokument: Juniorstav 2024: Proceedings 26th International Scientific Conference Of Civil Engineering, ISBN 978-80-86433-83-7
Instituce: Vysoké učení technické v Brně (web)
Informace o dostupnosti dokumentu: Plný text je dostupný v Digitální knihovně VUT.
Původní záznam: https://hdl.handle.net/11012/245410
Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-614334
Autoři: Jančíková, Andrea ; Ravaszová, Simona ; Dvořák, Karel ; Křištof, Michal
Typ dokumentu: Příspěvky z konference
Jazyk: eng
Nakladatel: Vysoké učení technické v Brně,Fakulta stavební
Abstrakt: The article is devoted to the study of the preparation and stabilization of pure cubic phase of tricalcium aluminate C₃A. The findings from the literature and several experimental trials have been summarized. Based on these findings, the synthesis of C₃A was realized, and high purity of this mineral was achieved. Furthermore, the influence of foreign ions, mainly in the form of potassium oxide K₂O combined with Na₂O in the form of sodium oxide on the crystal structure was investigated. The transformation of the cubic phase of C₃A into an orthorhombic phase was observed when the amount of these ions in the structure was changed.
Klíčová slova: C3A; clinker; crystal structure; high purity; Potassium oxide; tricalcium aluminate
Zdrojový dokument: Juniorstav 2024: Proceedings 26th International Scientific Conference Of Civil Engineering, ISBN 978-80-86433-83-7
Instituce: Vysoké učení technické v Brně (web)
Informace o dostupnosti dokumentu: Plný text je dostupný v Digitální knihovně VUT.
Původní záznam: https://hdl.handle.net/11012/245410
Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-614334
Záznam vytvořen dne 2024-05-12, naposledy upraven 2024-05-12.