Název:
Pressure pipe damage: Numerical estimation of point load effect
Autoři: Zouhar, Michal ; Hutař, Pavel ; Ševčík, Martin ; Náhlík, Luboš
Typ dokumentu: Příspěvky z konference
Konference/Akce: FDM 2012 - International Conference on Fracture and Damage Mechanics /11./, Xian (CN), 2012-09-12 / 2012-09-18
Rok: 2013
Jazyk: eng
Edice: Key Engineering Materials
Abstrakt: The most relevant loading conditions for real polymer pipe systems are not only internal pressure, but also loading caused by sand embedding including bending or different kinds of point loads. It has been shown that service lifetime of buried pipes can be reduced especially due to stress concentration caused by external point loads. If the pipe is loaded locally the stress is concentrated here and a crack can initiate at this position or the existing crack can be affected by corresponding stress redistribution. In the paper the effect of the hard indenter, Poisson's ratio, hoop stress level and pipe wall thickness on the crack shape was estimated using numerical simulations of the creep crack propagation based on finite element method. Relation between crack length and crack width was found and expressed by simple relationship. A deeper understanding of the point load effect in order to prevent unexpected failure of the pipelines is of paramount importance for pipeline design.
Klíčová slova: crack shape prediction; failure; point load; polymer pressure pipes; slow crack-growth; stress intensity factor
Číslo projektu: GAP108/12/1560 (CEP), GD106/09/H035 (CEP)
Poskytovatel projektu: GA ČR, GA ČR
Zdrojový dokument: Advances in Fracture and Damage Mechanics XI, ISBN 978-3-03785-463-1, ISSN 1013-9826
Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0280151
Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-373374
Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference
Autoři: Zouhar, Michal ; Hutař, Pavel ; Ševčík, Martin ; Náhlík, Luboš
Typ dokumentu: Příspěvky z konference
Konference/Akce: FDM 2012 - International Conference on Fracture and Damage Mechanics /11./, Xian (CN), 2012-09-12 / 2012-09-18
Rok: 2013
Jazyk: eng
Edice: Key Engineering Materials
Abstrakt: The most relevant loading conditions for real polymer pipe systems are not only internal pressure, but also loading caused by sand embedding including bending or different kinds of point loads. It has been shown that service lifetime of buried pipes can be reduced especially due to stress concentration caused by external point loads. If the pipe is loaded locally the stress is concentrated here and a crack can initiate at this position or the existing crack can be affected by corresponding stress redistribution. In the paper the effect of the hard indenter, Poisson's ratio, hoop stress level and pipe wall thickness on the crack shape was estimated using numerical simulations of the creep crack propagation based on finite element method. Relation between crack length and crack width was found and expressed by simple relationship. A deeper understanding of the point load effect in order to prevent unexpected failure of the pipelines is of paramount importance for pipeline design.
Klíčová slova: crack shape prediction; failure; point load; polymer pressure pipes; slow crack-growth; stress intensity factor
Číslo projektu: GAP108/12/1560 (CEP), GD106/09/H035 (CEP)
Poskytovatel projektu: GA ČR, GA ČR
Zdrojový dokument: Advances in Fracture and Damage Mechanics XI, ISBN 978-3-03785-463-1, ISSN 1013-9826
Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0280151
Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-373374
Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference
Záznam vytvořen dne 2018-03-09, naposledy upraven 2021-11-24.