Změkčování poly(3-hydroxybutyrátu)
Překlad názvu:
Softening of poly(3-hydroxybutyrate)
Autoři:
Brňák, Matúš ; Petruš, Josef (oponent) ; Kučera, František (vedoucí práce) Typ dokumentu: Bakalářské práce
Rok:
2016
Jazyk:
cze
Nakladatel: Vysoké učení technické v Brně. Fakulta chemická
Abstrakt: [cze][eng]
Bakalárska práca sa zaoberá zmäkčovaním PHB vybranými typmi zmäkčovadiel. Vplyv zmäkčovadiel je porovnávaný medzi sebou vzhľadom na ich vlastnosti a štruktúru. V teoretickej časti sú zhrnuté poznatky o zmäkčovaní polymérov a charakterizované jednotlivé druhy zmäkčovadiel. Experimentálna časť sa zaoberá samotným zmäkčovaním PHB v roztoku a tavenine. PHB bol rozpúšťaný v chloroforme a do vzniknutého roztoku boli pridávané zmäkčovadlá ATBC, TBC, ATEC, TEC, TOTM, PVAc a butylglykol s obsahom 30 hm %. Při zmäkčovaní v tavenine bola pripravená polymérna pasta s obsahom změkčovadla 70 hm % a 30 hm % PVAc. Zmes bola plastifikovaná v mixéri, pričom čas a želatinačná teplota boli stanovené experimentálne. Pomocou TGA boli stanovené hodnoty tepelnej degradácie pripravených vzoriek. DSC analýzou boli sledované hodnoty Tg, Tm a Xc. U vzoriek mäkčených v tavenine bola stanovená tvrdosť materiálu v stupnici Shore A a podľa Vickersa.
The bachelor thesis deals with the inluence of PHB softening, of selected types of plasticizers. The effect of the plasticizers are compared between themselves with regard to their properties and structure. The theoretical part summarizes the knowledge about softening polymers and characterized different types of plasticizers. The experimental part deals with PHB softening in the solution and in the melt. The plasticizers ATBC, TBC, ATEC, TEC, TOTM, PVAc and butylglycolate dilution containing 30 wt % were added to the PHB previously dissolved in chloroform. In the case of softening in the melt, a polymer paste was prepared, containing 70 wt % of plasticizers and 30 wt % of PVAc. The mixture was plasticized in a mixer, wherein time and temperature of the gelatinization were determined experimentally. Thermal degradation of preprared samples were specified by TGA. Values of Tg, Tm and Xc, was determined by DSC analysis. The samples plasticized in the melt were determined by the hardness of the material according to the Shore A scale and the Vickers scale.
Klíčová slova:
poly(3–hydroxybutyrátu); PVAc; zmäkčený PHB; zmäkčovadlá; štruktúra zmäkčovadiel; plasticizers; poly(3–hydroxybutyrate); PVAc; softened PHB; structure of plasticizers