Effects of .gamma.-irradiation on rheological properties of ultra-high molecular weight polyethylene melts
Překlad názvu:
Vliv .gamma.-záření na reologické vlastnosti tavenin ultravysokomolekulárního polyethylenu
Autoři:
Mikešová, Jana ; Nevoralová, Martina Typ dokumentu: Příspěvky z konference Konference/Akce: Novel Trends in Rheology, Zlín (CZ), 2005-06-09 / 2005-06-10
Rok:
2005
Jazyk:
eng
Abstrakt: [eng][cze] Ultra-high molecular weight polyethylene is widely used as material in orthopaedic implants. Melt rheology was used to evaluate the result of simultaneous crosslinking and chain scission process in the polymer, .gamma.-irradiated in the solid state. The predominant mechanism in the process was strongly influenced by irradiation dose and dose-rate. An important result was obtained for the polymer irradiated with the sterilization dose 25 kGy and stored in nitrogen when no significant degradation of the polymer was observed.Klinické problémy pacientů způsobené částicemi ultravysokomolekulárního polyethylenu uvolněnými do organismu z kloubních implantátů, vyvolaly zájem o radiační síťování tohoto polymeru. V polymeru po ozáření dochází jak k síťování tak i degradaci. Převahu jednoho z procesů je možné pozorovat meřením reologických vlastností taveniny polymeru. Testovány byly vlivy různých dávek záření a rychhostí ozařování. Důležitým závěrem práce bylo zjištění, že v polymeru ozářeném sterilizační dávkou 25 kGy a uchovávaném v dusíkové atmosféře nebyla pozorována degradace.
Klíčová slova:
rheology; UHMWPE Číslo projektu: GA106/04/1118 (CEP) Poskytovatel projektu: GA ČR Zdrojový dokument: Novel trends in rheology, ISBN 80-7318-303-X
Instituce: Ústav makromolekulární chemie AV ČR
(web)
Informace o dostupnosti dokumentu:
Dokument je dostupný v příslušném ústavu Akademie věd ČR. Původní záznam: http://hdl.handle.net/11104/0018152