Název: TEM and SEM study of precipitation hardened Cu-Co alloys after severe plastic deformation
Autoři: Buršík, Jiří ; Svoboda, Milan ; Král, Petr ; Dvořák, Jiří ; Sklenička, Václav
Typ dokumentu: Příspěvky z konference
Konference/Akce: NANOCON 2012. International Conference /4./, Brno (CZ), 2012-10-23 / 2012-10-25
Rok: 2012
Jazyk: eng
Abstrakt: The paper reports on preliminary results of microstructural study of Cu-2wt.%Co alloy processed by ECAP. The experimental alloy was cast and annealed at 1273 K for 10 hours followed by water cooling, resulting in the solid solution (the initial state). Further heat treatment was then applied to produce two-phase material with fine distribution of precipitates. ECAP was then conducted at room temperature on both the initial and the precipitation hardened states. Resulting microstructures were studied and characterized by microhardness testing, TEM observations and texture analysis by means of electron backscatter diffraction (EBSD) technique in SEM.
Klíčová slova: electron microscopy; microstructure; severe plastic deformation
Číslo projektu: GAP108/11/2260 (CEP)
Poskytovatel projektu: GA ČR
Zdrojový dokument: NANOCON 2012, 4th International Conference Proceedings, ISBN 978-80-87294-35-2

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0228232

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-166322


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference