Název: Compressive Creep Tests of An Aluminium Powder Composite Reinforced by Ceramic Particles
Autoři: Dvořák, Jiří ; Král, Petr ; Balog, M. ; Simančík, F. ; Sklenička, Václav
Typ dokumentu: Příspěvky z konference
Konference/Akce: METAL 2011 /20./, Brno (CZ), 2011-05-18 / 2011-05-20
Rok: 2011
Jazyk: eng
Abstrakt: The aim of this work is to study of a composite mixture of aluminium powders, to analyze of composite microstructure and mostly to describe the creep behaviour of composite in compression. The experimental material was based on Al powder matrix (Al 99%) about the particle size of less than 200 µm. This powder was mixtured with silicon carbide particles (SiC) having the size about 10 µm. The Al composite powder was prepared via conventional direct hot-extrusion (DE) at temperature 450°C. The microstructural investigations were performed using OM and SEM. It was found that DE process exhibits some breaking of carbide particles to size of range from 0.5 to 5 µm. Creep tests in compression were conducted at temperatures 423 -623 K and at applied stresses in the range from 60 to 100 MPa. Consequently, for an evaluation of controlling creep mechanisms an activation energy of creep and the stress exponent of the creep rate were determined.
Klíčová slova: aluminium powder; ceramic particles; creep
Číslo projektu: CEZ:AV0Z20410507 (CEP), KJB200410801 (CEP)
Poskytovatel projektu: GA AV ČR
Zdrojový dokument: Metal 2011, ISBN 978-80-87294-24-6

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0207856

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-109894


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference