Název: Magnetocrystalline anisotropy of Ni-Mn-Ga-Co-Cu martensite
Autoři: Rameš, Michal ; Straka, Ladislav ; Sozinov, A. ; Heczko, Oleg
Typ dokumentu: Příspěvky z konference
Konference/Akce: Studentská vědecká konference fyziky pevných látek a materiálů /11./, Praha (CZ), 20220912
Rok: 2022
Jazyk: eng
Abstrakt: The martensites of Heusler alloys based on Ni-Mn-Ga exhibit magnetically-induced reorientation resulting in giant field-induced strain. Up to 12% strain was observed in Ni-Mn-Ga-Co-Cu with 4 at.% of Co and Cu. The driving force of the phenomenon is the magnetocrystalline anisotropy. We studied evolution of the anisotropy with temperature and compositions using magnetiyation curve measurements in four different single crystalline Ni-Mn-Ga-Co-Cu and compared with non-doped Ni-Mn-Ga. The anisotropy of martensite decreases with increasing average doping (Co+Cu)/2 but it does not scale with tetragonal ratio or valence electron concentration.
Klíčová slova: Heusler alloys; magnetocrystalline anisotropy; martensite; Ni-Mn-Ga
Číslo projektu: GA21-06613S (CEP), LM2018096 (CEP)
Poskytovatel projektu: GA ČR, GA MŠk
Zdrojový dokument: Sborník příspěvků 11. Studentské vědecké konference fyziky pevných látek a materiálů, ISBN 978-80-01-07079-6

Instituce: Fyzikální ústav AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: https://hdl.handle.net/11104/0337801

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-512287


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Fyzikální ústav
Konferenční materiály > Příspěvky z konference
 Záznam vytvořen dne 2023-01-08, naposledy upraven 2023-03-28.


Není přiložen dokument
  • Exportovat ve formátu DC, NUŠL, RIS
  • Sdílet