Název: HIGH - TEMPERATURE CREEP BEHAVIOUR OF CAST COBALT-BASE SUPERALLOYS
Autoři: Dvořák, Jiří ; Král, Petr ; Kvapilová, Marie ; Hrbáček, Karel ; Sklenička, Václav
Typ dokumentu: Příspěvky z konference
Konference/Akce: Metal 2018 - International conference on metallurgy and materials /27./, Brno (CZ), 20180523
Rok: 2018
Jazyk: eng
Abstrakt: Two cast and heat-treated NbC and TaC – strengthened cobalt superalloys have been developed for a precision casting of spinner discs for glass wool industry. In this work constant load creep tests in tension were carried out in argon atmosphere at three testing temperature 900, 950 and 1000 °C and at the initial applied stresses ranged from 40 to 200 MPa. All the tests were continued until the final fracture. The results of creep testing were combined with microstructural and fractographic examinations by means of light and scanning electron microscopy. A mutual comparison of creep characteristics of the investigated superalloys under comparable creep loading conditions showed that NbC-strengthened superalloy exhibited longer creep life than TaC-strengthened one. Further, it was found that carbide precipitation is the primary strengthening mechanism in both cobalt-base superalloys under investigation and the amount, morphology\nand type of carbides have the decisive effect on the creep properties including creep damage and fracture processes. By contrast, NbC-superalloy exhibited a more brittle character of creep fracture mode than TaCstrengthened superalloy. This study was initiated to investigate in more details creep deformation processes and the effect of the creep microstructure and damage evolution on both investigated superalloys. The different behaviour and properties of studied superalloys were explained based on the received results of this study.
Klíčová slova: carbide precipitation; Co-based superalloys; creep tests; damage process; microstructure evolution
Číslo projektu: FV10699, LM2015069 (CEP), ED1.1.00/02.0068
Poskytovatel projektu: GA MPO, GA MŠk, GA MŠk
Zdrojový dokument: Metal 2018 - 27th International conference on metallurgy and materials, Conference Proceedings, ISBN 978-80-87294-84-0

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0291961

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-391454


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference
 Záznam vytvořen dne 2019-02-13, naposledy upraven 2019-10-20.


Není přiložen dokument
  • Exportovat ve formátu DC, NUŠL, RIS
  • Sdílet