Název: Interaction of Creep and High Cycle Fatigue of IN 713LC Superalloy
Autoři: Horník, V. ; Šmíd, Miroslav ; Hutař, Pavel ; Kunz, Ludvík ; Hrbáček, K.
Typ dokumentu: Příspěvky z konference
Konference/Akce: MSMF8. International Conference on Materials Structure and Micromechanics of Fracture /8./, Brno (CZ), 20160627
Rok: 2017
Jazyk: eng
Abstrakt: The study deals with the interaction of creep and high cycle fatigue of cast polycrystalline nickel-based superalloy IN 713LC at high temperatures. Previous works indicated that creep lifetime of superalloy structures was un-affected or even slightly increased in the cases with superimposed vibrations. The reason for this behaviour was not well described up to now. Therefore, set of fatigue tests was conducted at high mean stresses level to observe this phenomenon. The mean stress was kept constant while the stress amplitudes were selected in order to measure wide range of conditions from pure creep to pure fatigue. Fractographic analysis by scanning electron microscopy (SEM) was done with the aim to identify governing damage mechanisms for particular test conditions as a preliminary evaluation of conducted tests.
Klíčová slova: Creep-fatigue interaction; Fractography; High temperature; IN 713LC; Superalloy
Číslo projektu: TA04011525 (CEP), LM2015069 (CEP)
Poskytovatel projektu: GA TA ČR, GA MŠk
Zdrojový dokument: Materials Structure & Micromechanics of Fracture VIII, ISBN 978-3-03835-626-4, ISSN 1662-9779
Poznámka: Související webová stránka: https://www.scientific.net/SSP.258.595

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0276114

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-373287


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference