Název: Compressive creep testing of MoSi2-SiC nanocomposites
Autoři: Luptáková, Natália ; Ballóková, B. ; Dymáček, Petr
Typ dokumentu: Příspěvky z konference
Konference/Akce: ICMT 2015, Materiály a technologie ve výrobě speciální techniky /13./, Brno (CZ), 2015-05-20
Rok: 2015
Jazyk: eng
Abstrakt: The aim of this study is to investigate the creep resistance of molybdenum disilicide (MoSi2-SiC) based composites with different types of embedded particles. The materials were prepared via powder metallurgy using high temperature controlled reaction sintering (CRS). The creep experiments were performed in uniaxial compression at constant stress in the temperature range from 1273 K (1000 °C) to 1473 K (1200 °C) for applied stress from 50 to 100 MPa. Creep was tested by stepwise loading: in each step, the load was changed to a new value after steady state creep rate had been established. The applied stress dependences of the creep rate at different temperatures were analyzed in terms of stress exponent (n) and activation energy (Q). Possible rate-controlling mechanisms were suggested.
Klíčová slova: activation energy; compressive creep; creep test; MoSi2-SiC; stress exponent
Číslo projektu: ED1.1.00/02.0068
Poskytovatel projektu: GA MŠk
Zdrojový dokument: Materiály a technologie ve výrobě speciální techniky, ISBN 978-80-7231-999-2

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0249279

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-200403


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference