Study of behavior of concrete and cement based composite materials exposed to high temperatures
Bodnárová, L. ; Horák, D. ; Válek, J. ; Hela, R. ; Sitek, Libor
The paper describes possibilities of observation of behaviour of concrete and cement based composite material exposed to high temperatures. Nowadays, for large-scale tests of behaviour of concrete exposed to high temperatures, testing devices of certified fire testing stations in the Czech Republic and surrounding states are used. These tests are quite expensive. For experimental verification of smaller test specimens, a testing device was built at the Technical University in Brno, where tests of thermal loading of concrete tests specimens of various sizes can be carried out (dimensions up to 800 x 800 x 800 mm or slabs up to 1100 mm of length). The testing device opens new ways of observation of behaviour of concrete and cement based composite materials exposed to high temperatures as well as preparation of specimens for observation of interaction of water jet and concrete degraded by action of high temperatures.
Plný tet: UGN_0398264 -  DOC
Plný text: content.csg - DOC
|
|
Vliv poklesu cen ropy a zemního plynu od roku 2014 na katarskou ekonomiku
Šamánek, Ondřej ; Stuchlíková, Zuzana (vedoucí práce) ; Hasík, Gabriel (oponent)
Bakalářská práce se zaobírá vlivem pádu cen ropy a zemního plynu, který postihl svět v červnu roku 2014, na ekonomiku Kataru. Hlavním cílem práce je zjistit, jak a do jaké míry pokles cen zmíněných komodit ovlivnil ekonomické ukazatele a chování státu i jednotlivých firem operujících v postihnutém odvětví. Zvolený problém je řešen pomocí metody časové komparace, u níž jsou hodnoty relevantních ekonomických ukazatelů porovnány před a po krizi, či vypracovanou případovou studií, u které je situace analyzována na příkladu katarské firmy operující v postiženém odvětví. Ze zkoumání vyplývá, že pád cen ropy a zemního plynu na ekonomiku Kataru vliv měl. Země se rok po snížení cen potýkala se snížením HDP či propadem rozpočtového salda, postižená firma v odvětví zase vykazovala pokles počtu udělených zakázek či rekordní množství zrušených výběrových řízení. Závěry z práce vyplývající lze do jisté míry užít i na ostatní ropné exportéry Perského zálivu, kteří s Katarem sdílejí podobné rysy.
|
|
Adaptace marketingové strategie společnosti Chipotle na českém trhu
Hofmannová, Veronika ; Král, Petr (vedoucí práce) ; Janecký, Vlastimil (oponent)
Diplomová práce se zabývá fastfoodovým řetězcem Chipotle, známým především ve Spojených státech amerických, a jeho potenciálním vstupem na český trh. Analyzuje marketingovou strategii společnosti a řeší její adaptaci pro český trh. Konkurenční výhodou společnosti je používání lokálních bio surovin, proto ve své diplomové práci zkoumám zájem Čechů o mexickou kuchyni a udržitelný rozvoj. Cílem mé diplomové práce je analýza marketingové strategie mexického fast foodového řetězce Chipotle a následná adaptace marketingového mixu na českém trhu.
|
|
Changes in structure and phase composition in the surface of tram rail
Švábenská, Eva ; Roupcová, Pavla ; Schneeweiss, Oldřich
We have investigated structure and phase composition of surface layer of tram rails after long time running and the results were compared with those obtained on the original part of material. Changes due to effects of severe plastic deformation together with thermal shocks by friction process were expected. The information about structure and phase composition was obtained by optical and scanning electron microscopy, X-Ray Powder Diffraction, Mössbauer Spectroscopy and Glow Discharge Emission Spectroscopy (GDOES) and this was completed by microhardness measurements. The results show that the surface layer in comparison with the original material exhibits important changes in grain structure, an increase in microhardness and high content of iron oxide and hydrooxides. According to the depth profile of the chemical composition measured by GDOES there is an increase in carbon content in the surface layer which can be effect of up-hill diffusion.
|
|
STRAIN ENGINEERING OF THE ELECTRONIC STRUCTURE OF 2D MATERIALS
del Corro, Elena ; Peňa-Alvarez, M. ; Morales-García, A. ; Bouša, Milan ; Řáhová, Jaroslava ; Kavan, Ladislav ; Kalbáč, Martin ; Frank, Otakar
The research on graphene has attracted much attention since its first successful preparation in 2004. It possesses many unique properties, such as an extreme stiffness and strength, high electron mobility, ballistic transport even at room temperature, superior thermal conductivity and many others. The affection for graphene was followed swiftly by a keen interest in other two dimensional materials like transition metal dichalcogenides. As has been predicted and in part proven experimentally, the electronic properties of these materials can be modified by various means. The most common ones include covalent or non-covalent chemistry, electrochemical, gate or atomic doping, or quantum confinement. None of these methods has proven universal enough in terms of the devices' characteristics or scalability. However, another approach is known mechanical strain/stress, but experiments in that direction are scarce, in spite of their high promises.\nThe primary challenge consists in the understanding of the mechanical properties of 2D materials and in the ability to quantify the lattice deformation. Several techniques can be then used to apply strain to the specimens and thus to induce changes in their electronic structure. We will review their basic concepts and some of the examples so far documented experimentally and/or theoretically.
|
|
Micro-electromembrane extraction across multiple aqueous and organic phases for selective pretreatment of raw biological samples
Kubáň, Pavel ; Boček, Petr ; Seip, K. F. ; Gjelstad, A. ; Pedersen-Bjergaard, S.
Micro-electromembrane extraction (μ-EME) across multiple aqueous and organic\nsolutions was developed for selective extractions of various analytes from untreated\nbiological samples. The novel approach requires μL volumes of samples and organic\nsolvents, which form consecutive immiscible plugs in a transparent polymeric capillary\nand the extraction process is accelerated by application of d.c. voltage. Number of the\nplugs, their composition, volume and sequence in the extraction capillary can be chosen\nspecifically for each particular application and high variability and selectivity of the\nextraction process can be achieved. In this contribution, we demonstrate suitability of\na five-phase μ-EME system for simultaneous extractions of cations and anions from\nurine and for selective extractions of basic analytes based on their acid-base strength\nfrom plasma.
|
|
ELECTRON BEAM REMELTING OF PLASMA SPRAYED ALUMINA COATINGS
Matějíček, Jiří ; Veverka, J. ; Čížek, J. ; Kouřil, J.
Plasma sprayed alumina coatings find numerous applications in various fields, where they enhance the properties of the base material. Examples include thermal barriers, wear resistance, electrical insulation, and diffusion and corrosion barriers. A typical structure of plasma sprayed coatings, containing a multitude of voids and imperfectly bonded interfaces, gives them unique properties - particularly low thermal conductivity, high strain tolerance, etc. However, for certain applications such as permeation barriers or wear resistance, these voids may be detrimental.\nThis paper reports on the first experiments with remelting of plasma sprayed alumina coatings by electron beam technology, with the purpose of densifying the coatings and thereby eliminating the voids. Throughout the study, several parameters of the e-beam device were varied - beam current, traverse velocity and number of passes. The treated coatings were observed by light and electron microscopy and the thickness, structure and surface morphology of the remelted layer were determined and correlated with the process parameters. Based on the first series of experiments, the e-beam settings leading to dense and smooth remelted layer of sufficient thickness were obtained. In this layer, a change of phase composition and a marked increase in hardness were observed.\n
|
|
SAN MINN (ANEB) UMĚLEC, KTERÝ DÁVÁ PŘEDNOST TVORBĚ A OBRAZŮM PŘED SVÝM ŽIVOTEM
Zeya, Pyin Nyar ; JANEČEK, Vít (vedoucí práce) ; VOJTĚCHOVSKÝ, Miloš (oponent)
Nikdo nemůže ovládat svobodné myšlení a inspiraci umělce. Přestože jeho obrazy a tvorba byly vystaveny velkému tlaku a na nátlak shora zakázány, jejich umělecká hodnota nikdy neklesla. Proto píši tuto práci.
San Minn vystoupil zbarmského malířského mainstreamu a nikdy nenamaloval komerční obraz. Je stále věren své víře v umění a malbu a přichází vždy s novými způsoby, jak přistoupit malování. Jeho tvorba se podstatně odlišuje od jeho souputníků a jeho styl se výrazně liší. V barmském malířství je unikátním jevem. Naskytla se mi možnost studovat jeho styl, myšlenky, způsob uvažování a jeho odhodlání s jakým umění vytváří.
Moje práce má za cíl ukázat život umělce a malíře, který vyrostl a žil 50 let pod vojenskou nadvládou, a skrze pohled na jeho případ popsat vývoj a stav výtvarné scény v Barmě. Zprostředkuji tak nejen zájemcům o malbu, ale všem ostatním čtenářům vhled do barmského malířství a místní umělecké scény. Doufám, že moje práce tak bude vhledem prospěšným a barvitým.
Zdá se, že jakožto malíř, San Minn chce, aby jeho publikum cítilo a zažilo jeho práce, ale jen zřídka odhaluje svůj osobní život, který se odvíjí za jeho plátny. Pro mě je tato práce zároveň i příležitostí jeho osobní rovinu alespoň trochu poodkrýt na následujících stránkách.
xxxxxxxxx
Cíl Práce
Má práce může být zajímavá pro každého, kdo se zajímá o současnou uměleckou scénu Barmy (Myanmaru).
Umožňuje čtenáři, aby se dočetl o jednom z nejslavnějších a nejvýznamnějších umělců a uměleckých směrů v Barmě (Myanmaru). Jeho malby jsou svědectvím o více než 40 let dlouhé cestě pod dohledem cenzury, avšak na každém kroku ukazují na jeho nebojácnost řešit politické a sociální otázky.
Mnohé z uměleckých děl San Minna jsou autobiografické, vytváří břitký sociální komentář k populární kultuře a zrcadlí sociální hodnoty, stejně jako situace, které jejich autor prožíval.
xxxxxxxxxxxx
|
|
Využití nově syntetizovaného amocharu ke stabilizaci a sorpci kovů a metaloidů.
Ouředníček, P. ; Trakal, L. ; Komárek, M. ; Pohořelý, Michael
Možnost sanace půd, která je většinou založena na principu stabilizace a imobilizace potenciálně rizikových látek, je v posledních letech intenzivně studovanou a zkoumanou problematikou. Jedním z takovýchto stabilizačních činidel je i biochar, tedy forma aktivního uhlí, která má schopnost poutat na svůj povrch celou řadu kontaminantů včetně právě kovů a metaloidů. Biochary mají obecně vysoce aktivní povrch a přítomnost různých funkčních skupin (např. COO–) zodpovědných za tvorbu chelátů a alkalických prvků (Ca2+, K+, Na+ a Mg2+) reprezentující kationtovou výměnu; v kombinaci s vysokými hodnotami pH (7,00 až 10,0) poukazují na jejich efektivní sorpční kapacitu vázat na svůj povrch kovy a metaloidy z roztoku (z půdní vody), zejména pak v kyselých půdách (tedy v oblastech postižených intenzivní důlní činností). Dále lze sorpční účinnost biocharů ještě zvýšit/vylepšit (zejména pak v případech odstraňování As (V) nebo Cr (VI)) a to pomocí různých modifikací. A právě modifikací biocharu pomocí amorfního oxidu manganu (AMO), byl vytvořen nový sorbent AMOchar. Produkt byl připraven přidáváním biocharu přímo do roztoku reaktantů při syntéze AMO. Samotný AMOchar je tak tvořen především Mn-oxaláty, které jsou přítomny ve formě povlaků na povrchu částic biocharu. Sorpční účinnost tohoto sorbentu pak byla i přes poměrně zásadité pH AMOcharu vysoká pro všechny testované rizikové prvky. Konkrétně byla sledována vysoká sorpce nejen pro Pb (téměř 99 %) a Cd (51,2 %) ale i pro As (91,4 %). Modifikace biocharu pomocí AMO též signifikantně snížila extrakci Mn, díky čemuž by nemělo, v případě reálného používání tohoto sorbentu pro sanaci půd, docházet k post-kontaminaci půdy právě manganem, který se uvolňuje z Mnoxalátů při rozpouštění jinak vysoce účinného sorbentu AMO.
Plný tet: SKMBT_22316111113040 -  PDF
Plný text: content.csg - PDF
|
|
Plazmové stříkání z kapalné fáze: interakce kapaliny s proudem plazmatu a vznik nástřiku
Tesař, Tomáš ; Mušálek, Radek ; Medřický, Jan ; Lukáč, František
Plazmové stříkání z kapalné fáze je rychle se rozvíjejícím odvětvím žárového stříkání. Hybnou silou vývoje jsou unikátní vlastnosti, které vrstvy deponované z kapalné fáze nabízejí, jako je vysoká tvrdost, vysoká odolnost vůči tepelným šokům či nízká tepelná a elektrická vodivost. Klíčovým faktorem ovlivňujícím výsledný vzhled a vlastnosti vyrobeného nástřiku je zvolený vstupní materiál, kterým může být suspenze jemného prášku či roztok. Parametry dané suspenze (koncentrace pevné fáze, viskozita, povrchové napětí, chemické složení, atd.) či roztoku (zejména koncentrace) pak ovlivňují interakci s proudem plazmatu, která má na výslednou mikrostrukturu zásadní vliv. Tento příspěvek přibližuje problematiku interakce kapalného vstupního materiálu s plazmatem a ukazuje možnosti studia mechanismů růstu nástřiku.
|
host ::