EFFECT OF STEEL COMPOSITION ON ITS BEHAVIOUR IN THE LIQUID LEAD ENVIRONMENT
Pazderova, M. ; Hojná, A. ; Vít, J. ; Hadraba, Hynek ; Čižek, J.
Ferritic-martensitic Eurofer-97 and oxide dispersion strengthened (ODS) Eurofer steels are potential candidates for structural applications in advanced nuclear reactors. Influence of scandium, yttrium, and aluminum addition was studied at 600 degrees C using 10-6 wt.% oxygen concentration. Microstructure and corrosion behaviour was evaluated after 500 h and 1000 h of exposure to liquid lead. Microscopical investigation identified oxidation, solution- based attack, and Pb penetration into the material. Addition of scandium and aluminum changed the mechanism of corrosion attack. Eurofer-97 was partially protected by outer oxide and inner oxidation and Pb penetration was found. In contrast ODS-Eurofer steels after 1000 h of exposure showed mainly inner oxidation and SBA including Pb penetration into the steel. The inner oxidation consisted of Pb+Cr-O and Cr-O+Al-O layers mixture. Degradation of ODS steel was significantly lower than Eurofer-97. It seems that the inner oxidation layer beneath the surface did not prevent the Pb penetration but protected the surface from dissolution.
|
|
|
Impact of the Number of Measurements on Result Distortion
Kuchařík, Jan ; Šimek, Antonín
This study investigates the distortion of results due to the number of corrosion current measurements. Samples were prepared by pressing and subsequently sintering iron and magnesium powders. The samples were then immersed in an SBL solution at 37 °C. Measurements took place over 23 days. For two samples, measurements were taken each time, while the remaining samples were measured in sequence on their respective days.
|
|
|
Voltametrická detekce 27-hydroxycholesterolu na borem dopované diamantové elektrodě
Michnová, Kristýna ; Schwarzová, Karolina (vedoucí práce) ; Nesměrák, Karel (oponent)
Cílem této bakalářské práce bylo studium voltametrického chování 27-hydroxycholesterolu za využití borem dopované diamantové elektrody. Byl zkoumán vliv několika faktorů na proudovou odezvu 27-hydroxycholesterolu: vliv základního elektrolytu, koncentrace kyseliny chloristé, rychlosti polarizace, obsahu vody a vliv pH. Studium bylo prováděno metodou cyklické voltametrie v prostředí kyseliny chloristé nebo v prostředí chloristanu sodného v acetonitrilu. 27-hydroxycholesterol poskytuje v prostředí 0,1 mol l-1 kyseliny chloristé v acetonitrilu (obsah vody 0,43 %) a 0,1 mol l-1 chloristanu sodného v acetonitrilu proudovou odezvu v anodické oblasti s potenciálem okolo +1450 mV vs. Ag/0,01 mol l-1 AgNO3 v 1 mol l-1 NaClO4 v acetonitrilu. Dále byla naměřena koncentrační závislost metodou diferenční pulzní voltametrie s limitem detekce (LOD) stanoveným na 2,71 μmol l-1 a limitem stanovitelnosti (LOQ) stanoveným na 9,04 μmol l-1 . Bylo prokázáno, že metoda voltametrie s lineárním nárůstem potenciálů nedosahuje srovnatelných limitních hodnot. Klíčová slova 27-hydroxycholesterol, borem dopovaná diamantová elektroda, oxidace, oxysteroly, voltametrie
|
|
| |
|
|
Reaction Mechanisms of Psychoactive Compounds
Sokolová, Romana ; Beneš, Marek ; Jiroušková, Eliška ; Degano, I.
The reaction mechanism of selected new psychoactive substances (NPS) 4-methylpentedrone and 2-(((4-ethyl-2,5-dimethoxyphenethyl)amino)methyl)phenol was investigated based on their\nelectrochemical and spectroelectrochemical properties. Both drugs were examined by means of cyclic voltammetry using diagnostic parameters for particular reaction schemes, UV/Vis, and IR\nspectroelectrochemistry. Since water participates in the redox mechanism of both studied compounds, the reaction mechanism was studied under a controlled amount of water in an\nacetonitrile environment.
|
|
|
Oxidation behavior adjustment for TiAl intermetallics by Al-Y multilayers
Handrk, Jiří ; Tkachenko, Serhii (oponent) ; Jan, Vít (vedoucí práce)
Mechanical properties of titanium aluminide Ti-46Al-7Nb-0.7Cr-0.1Si-0.2Ni are constant above 700°C. Alloy oxidize above this temperature. Aim of this thesis is to verify a possibility to influences the oxidation properties of intermetallic TiAl based by metal multilayer from Y and Al. Layers The coating was done by PVD technique. Samples were coated by pure yttrium or combination yttrium and aluminium. Samples were annealed at 700°C and 900°C for annealing temperature influence. Quality of layers were investigated by scratch test, EDS analysis. Samples were oxidized isothermally at 900°C for 100hrs. After oxidation all samples were subjected oxide surface evaluation, fracture bending tests after which fracture surface and adherence of the oxide scale were evaluated. The chemical composition of oxide scales was measured using EDS on metallographic specimen. Any layers with or without annealing not shown positive oxidation properties. Higher temperature of annealing shown better adhesity but worst three point bend test results.
|
|
| |
|
| |
|
|
Problematika sorpcí fenolů z odpadních vod
Židek, Michal ; Pavlovský,, Jiří (oponent) ; Doležalová Weissmannová, Helena (vedoucí práce)
Bakalářská práce pojednává o problematice fenolů v odpadních vodách. V teoretické části je uvedena základní charakteristika fenolu, jeho účinky a výskyt. Dále jsou v práci rozebírány metody odstraňování fenolu z odpadních vod a důraz je kladen na způsob odstraňování fenolů s využitím mechanismu adsorpce. Součástí práce je analýza současných adsorbentů využívaných při odstraňování fenolu z vodného prostředí a vlastnosti těchto materiálů se zaměřením na materiály na základě jílových minerálů. Experimentální část se zabývá možností odstraňování fenolu z vodného prostředí mechanismem sorpce na bentonitu 75 za různých podmínek pH.
|
|
|
Selektivní hydrogenace/oxidace CVD grafenu pomocí AFM
Přikryl, Vojtěch ; Švarc, Vojtěch (oponent) ; Bartošík, Miroslav (vedoucí práce)
Grafen je perspektivní materiál v elektronice, z důvodu své vysoké pohyblivosti nosičů náboje. Má-li však být aplikovatelný v praxi, je třeba u něj otevřít zakázaný pás. Jedním ze způsobů jak toho dosáhnout, je úprava grafenu hydrogenací nebo oxidací. Tato práce se zabývá možností využití AFM k lokální hydrogenaci/oxidaci grafenu v závislosti na napětí mezi hrotem a vzorkem. Přítomnost hydrogenace/oxidace byla zkoumána pomocí Kelvinovy silové mikroskopie a Ramanovy spektroskopie. Možnost oxidace byla potvrzena, ale hydrogenace potvrzena nebyla.
|