Thermal degradation of insulation materials from the cable industry
Kučera, Filip ; Krbal, Michal (referee) ; Pelikán, Luděk (advisor)
The aim of this bachelor thesis is to get acquainted with the properties and parameters of insulation materials of various types (PVC, PE). Measure these properties with a Tettex 2830/2831. Perform a theoretical analysis of the aging of insulating materials and propose a procedure for the formation of thermal degradation. Finally, find out how the properties of insulating materials, electrical strength and mechanical properties change due to thermal degradation.
|
|
| |
|
|
Testing of processing stability of PP-g-IA
Hampapa, Břetislav ; Tocháček, Jiří (referee) ; Kučera, František (advisor)
The Bachelor’s study is interested in processing stability of polypropylene grafting with Itaconic anhydride. A present knowledge about thermal degradation of Itaconic derivatives was summarized in theoretical part. Samples were prepared by multiple extrusions technique from virgin PP (Borsodchem, Hungary) and PP-g-IA. Die temperature 230 °C, processing time 4 minutes by 20 RPM. Qualitative and quantity analysis was made by FT-IR spectroscopy.
|
|
|
Morphogenesis and Viscoelastic Properties of Dimethacrylate Networks
Bystřický, Zdeněk ; Lehocký, Marián (referee) ; Bradna, Pavel (referee) ; Jančář, Josef (advisor)
Tato dizertační práce se zabývá studiem morfogeneze dimethakrylátových sítí. V práci byly využity zjednodušené systémy založené na monomerech, které bývají typicky využívány jako složky matric pryskyřičných kompozitních materiálů využívaných v oblasti záchovné stomatologie. Kinetika a mechanismy formování polymerních sítí byly studovány především s ohledem na strukturu jednotlivých monomerů, jejich vzájemný molární poměr a koncentraci iniciačního systému využitého pro radikálovou polymeraci. Vypočtené profily konverze funkčních skupin a reakčních rychlostí byly využity jako základ pro pochopení a interpretaci mechanismů morfogeneze sítí a porovnání se známými modely. Dále byla studována kinetika termické degradace, která je s morfologií vytvrzených sítí přímo spjata. V rámci takto charakterizovaných systémů byla stanovena teplotní závislost dynamického modulu a byl popsán vztah mezi supra-molekulární strukturou dimethakrylátových sítí a jejich viskoelastickou odezvou v daném teplotním rozmezí. Kinetika polymerace byla studována pomocí diferenční kompenzační foto-kalorimetrie (DPC) a infračervené spektroskopie (FTIR). Proces termické degradace byl analyzován pomocí termo-gravimetrické analýzy (TGA). Viskoelastické parametry byly charakterizovány pomocí dynamicko-mechanické analýzy (DMA). Reaktivita jednotlivých systémů je přímo odvozena od molekulární struktury monomerů, která ovlivňuje mobilitu reagujících složek v průběhu polymerace. Kinetika polymerace je řízena především difúzí, přičemž její rychlost je dána tuhostí monomerní páteře, koncentrací funkčních skupin a vlivem fyzikálních interakcí. Omezená mobilita rostoucích řetězců, postranních funkčních skupin i samotných monomerů vede k monomolekulární terminaci makro-radikálů a omezení stupně konverze funkčních skupin. Vzhledem k tomu, že k zásadnímu omezení mobility dochází již v počáteční fázi polymerace, tj. v bodu gelace, je případná termodynamická nestabilita vedoucí k fázové separaci polymerujícího systému potlačena a proces kopolymerace je ve své podstatě náhodný. To bylo prokázáno i prostřednictvím identifikace jedné teploty skelného přechodu u charakterizovaných kopolymerů. Heterogenní charakter morfogeneze je spjat s rozdílnou reaktivitou postranních funkčních skupin. V počátečních fázích polymerace dochází k propagaci reakcí postranní funkční skupiny s radikálem na stejném rostoucím řetězci, což vede ke vzniku tzv. primárního cyklu. Pravděpodobnost cyklizace souvisí především s flexibilitou monomerní páteře. Heterogenita polymerace je charakterizována vznikem vnitřně zesítěných struktur, tzv. mikrogelů, a jejich následným spojováním. Tuhost monomeru naopak přispívá k vyšší efektivitě zesítění a více homogenní morfologii vytvrzené sítě. Heterogenita dimethakrylátových sítí se odráží v mechanismu termické degradace, přičemž přítomnost strukturně odlišných domén vede k rozkladu ve dvou krocích. Průběh soufázového modulu a teplota skelného přechodu korelují s tuhostí polymerních sítí, efektivitou zesítění a přítomností fyzikálních interakcí, které vyztužují strukturu sítě nad rámec kovalentního zesítění. Heterogenní morfologie sítí se projevuje rozšiřováním spektra relaxačních časů. Experimentální data jsou v kvalitativní shodě s existujícími numerickými modely popisujícími kinetiku radikálové polymerace multifunkčních monomerů.
|
|
|
Thermal degradation of insulation materials from the cable industry
Kučera, Filip ; Krbal, Michal (referee) ; Pelikán, Luděk (advisor)
The aim of this bachelor thesis is to get acquainted with the properties and parameters of insulation materials of various types (PVC, PE). Measure these properties with a Tettex 2830/2831. Perform a theoretical analysis of the aging of insulating materials and propose a procedure for the formation of thermal degradation. Finally, find out how the properties of insulating materials, electrical strength and mechanical properties change due to thermal degradation.
|
|
|
Morphogenesis and Viscoelastic Properties of Dimethacrylate Networks
Bystřický, Zdeněk ; Lehocký, Marián (referee) ; Bradna, Pavel (referee) ; Jančář, Josef (advisor)
Tato dizertační práce se zabývá studiem morfogeneze dimethakrylátových sítí. V práci byly využity zjednodušené systémy založené na monomerech, které bývají typicky využívány jako složky matric pryskyřičných kompozitních materiálů využívaných v oblasti záchovné stomatologie. Kinetika a mechanismy formování polymerních sítí byly studovány především s ohledem na strukturu jednotlivých monomerů, jejich vzájemný molární poměr a koncentraci iniciačního systému využitého pro radikálovou polymeraci. Vypočtené profily konverze funkčních skupin a reakčních rychlostí byly využity jako základ pro pochopení a interpretaci mechanismů morfogeneze sítí a porovnání se známými modely. Dále byla studována kinetika termické degradace, která je s morfologií vytvrzených sítí přímo spjata. V rámci takto charakterizovaných systémů byla stanovena teplotní závislost dynamického modulu a byl popsán vztah mezi supra-molekulární strukturou dimethakrylátových sítí a jejich viskoelastickou odezvou v daném teplotním rozmezí. Kinetika polymerace byla studována pomocí diferenční kompenzační foto-kalorimetrie (DPC) a infračervené spektroskopie (FTIR). Proces termické degradace byl analyzován pomocí termo-gravimetrické analýzy (TGA). Viskoelastické parametry byly charakterizovány pomocí dynamicko-mechanické analýzy (DMA). Reaktivita jednotlivých systémů je přímo odvozena od molekulární struktury monomerů, která ovlivňuje mobilitu reagujících složek v průběhu polymerace. Kinetika polymerace je řízena především difúzí, přičemž její rychlost je dána tuhostí monomerní páteře, koncentrací funkčních skupin a vlivem fyzikálních interakcí. Omezená mobilita rostoucích řetězců, postranních funkčních skupin i samotných monomerů vede k monomolekulární terminaci makro-radikálů a omezení stupně konverze funkčních skupin. Vzhledem k tomu, že k zásadnímu omezení mobility dochází již v počáteční fázi polymerace, tj. v bodu gelace, je případná termodynamická nestabilita vedoucí k fázové separaci polymerujícího systému potlačena a proces kopolymerace je ve své podstatě náhodný. To bylo prokázáno i prostřednictvím identifikace jedné teploty skelného přechodu u charakterizovaných kopolymerů. Heterogenní charakter morfogeneze je spjat s rozdílnou reaktivitou postranních funkčních skupin. V počátečních fázích polymerace dochází k propagaci reakcí postranní funkční skupiny s radikálem na stejném rostoucím řetězci, což vede ke vzniku tzv. primárního cyklu. Pravděpodobnost cyklizace souvisí především s flexibilitou monomerní páteře. Heterogenita polymerace je charakterizována vznikem vnitřně zesítěných struktur, tzv. mikrogelů, a jejich následným spojováním. Tuhost monomeru naopak přispívá k vyšší efektivitě zesítění a více homogenní morfologii vytvrzené sítě. Heterogenita dimethakrylátových sítí se odráží v mechanismu termické degradace, přičemž přítomnost strukturně odlišných domén vede k rozkladu ve dvou krocích. Průběh soufázového modulu a teplota skelného přechodu korelují s tuhostí polymerních sítí, efektivitou zesítění a přítomností fyzikálních interakcí, které vyztužují strukturu sítě nad rámec kovalentního zesítění. Heterogenní morfologie sítí se projevuje rozšiřováním spektra relaxačních časů. Experimentální data jsou v kvalitativní shodě s existujícími numerickými modely popisujícími kinetiku radikálové polymerace multifunkčních monomerů.
|
|
| |
|
| |
|
|
Testing of processing stability of PP-g-IA
Hampapa, Břetislav ; Tocháček, Jiří (referee) ; Kučera, František (advisor)
The Bachelor’s study is interested in processing stability of polypropylene grafting with Itaconic anhydride. A present knowledge about thermal degradation of Itaconic derivatives was summarized in theoretical part. Samples were prepared by multiple extrusions technique from virgin PP (Borsodchem, Hungary) and PP-g-IA. Die temperature 230 °C, processing time 4 minutes by 20 RPM. Qualitative and quantity analysis was made by FT-IR spectroscopy.
|