Název: Vliv přídavku krátkých para-aramidových vláken na vlastnosti ultravysokohodnotného cementového kompozitu
Překlad názvu: Influence of short para-aramid fibers addition on the properties of ultra-high performance cement composite
Autoři: Tandlich, Dávid ; Šoukal, František (oponent) ; Bocian, Luboš (vedoucí práce)
Typ dokumentu: Bakalářské práce
Rok: 2023
Jazyk: slo
Nakladatel: Vysoké učení technické v Brně. Fakulta chemická
Abstrakt: [slo] [eng]
V tejto bakalárskej práci bolo preskúmané využitie p-aramidových vlákien v ultravysokohodnotných cementových kompozitoch. Tieto vlákna boli použité ako samostatná výstuž, ale aj ako hybridná výstuž v kombinácii s oceľovými vláknami. Povrch oboch typov vlákien bol analyzovaný na SEM. Okrem kompozitu s p-aramidovými vláknami a hybridného kompozitu bol pripravený aj referenčný kompozit s oceľovými vláknami a matrica bez obsahu vlákien. Pripravené telesá boli podrobené testom pevnosti v tlaku a pevnosti v ťahu za ohybu. Na vybraných vzorkách bola analyzovaná lomová plocha na SEM. Ukázalo sa, že nie je možné jednoznačne určiť kompozit s najlepšími mechanickými vlastnosťami, nakoľko sa smerodajné odchýlky hybridného a referenčného kompozitu vo výsledkoch prekrývajú. Priemerne však vykazoval najlepšie mechanické vlastnosti hybridný kompozit. Kompozit, ktorý obsahoval len p-aramidové vlákna vykazoval výrazne nižšiu pevnosť v tlaku aj v ťahu za ohybu v porovnaní s referenčným kompozitom. Bolo zistené, že p-aramidové vlákna samostatne neprevyšovali účinok oceľových vlákien. Problém predstavovala aj tendencia p-aramidových vlákien výrazne znižovať rozliv a tvoriť v matrici zhluky, čo negatívne vplývalo na výsledné vlastnosti kompozitu. Na druhú stranu, použitie p-aramidových vlákien v kombinácii s oceľovými sa javilo ako výhodné, nakoľko výsledky ukázali, že vďaka p-aramidovým vláknam došlo k miernemu dovystuženiu matrice a zlepšeniu mechanických vlastností v rámci smerodajných odchýlok. In this bachelor's thesis, the use of p-aramid fibers in ultra-high performance cementitious composites was investigated. These fibers were used as a separate reinforcement, but also as a hybrid reinforcement in combination with steel fibers. The surface of both types of fibers was analyzed by SEM. In addition to the composite with p-aramid fibers and the hybrid composite, a reference composite with steel fibers and a matrix without fibers were also prepared. The prepared objects were tested in compressive strength and flexural tensile strength. Furthermore, the fracture surface on the selected bodies was analyzed by SEM. It turned out that it is not possible to clearly determine the composite with the best mechanical properties, as the standard deviations of hybrid and reference composite overlap. However, based on average values, the hybrid composite showed the best mechanical properties. The composite that contained only p-aramid fibers showed significantly lower compressive and flexural strength both compared to the reference composite. Results showed that p-aramid fibers alone did not exceed the effect of steel fibers. A problem was the tendency of p-aramid fibers to decrease a spillage and to form clusters in the matrix, which negatively affected the resulting properties of the composite. However, the use of p-aramid fibers in combination with steel fibers appeared to be advantageous, as it was found out that thanks to p-aramid fibers there was a slight reinforcement of the matrix and an improvement of the mechanical properties within the standard deviations.
Klíčová slova: compressive strength; fiber hybridization; flexural strength; reactive powder concrete; Ultra-high-performance concrete

Instituce: Vysoké učení technické v Brně (web)
Informace o dostupnosti dokumentu: Plný text je dostupný v Digitální knihovně VUT.
Původní záznam: http://hdl.handle.net/11012/210746

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-529029


Záznam je zařazen do těchto sbírek:
Školství > Veřejné vysoké školy > Vysoké učení technické v Brně
Vysokoškolské kvalifikační práce > Bakalářské práce