Termofyzikálne a elektrické vlastnosti keramík na báze illitu

Csáki, Štefan

CSÁKI, Štefan: Thermophysical and electrical properties of illite-based ceramics. [Doctoral thesis]. Constantine the Philosopher University in Nitra. Faculty of Natural Sciences. Charles University. Faculty of Mathematics and Physics. Supervisor: prof. RNDr. Libor Vozár, CSc. (Constantine the Philosopher University in Nitra), doc. Ing. Patrik Dobroň, PhD. (Charles University). Nitra & Prague, 2018. 107 p. Illitic clays are of special importance in the ceramic industry. Therefore, a deep knowledge of the thermophysical processes, as well as the electric properties, is of special importance. The illitic clay originated in Northeastern Hungary was used in this thesis. The reactions, occurring during firing, were studied using thermal analyses (Differential thermal analysis, Thermogravimetry, Thermodilatometry) and special attention was paid to the measurement of the electrical conductivity (both DC and AC). Up to 250 řC, where the removal of the physically bond water (PBW) takes place, the dominant charge carriers were the H+ and OH- ions. After the PBW was removed, Na+ and K+ ions became the dominant charge carriers. During dehydroxylation (450 - 750 řC) H+ and OH- ions were freed from the illite structure, which supported the electrical conduction in the samples. At ~ 970 řC glassy phase appeared...

host :: přihlásit Digitální repozitář
		Hledej		Nový záznam		Nápověda		O repozitáři