Název: Control of intergranular oxidation by thermal treatment
Autoři: Rothová, Věra ; Buršík, Jiří ; Svoboda, Milan
Typ dokumentu: Příspěvky z konference
Konference/Akce: METAL 2009. Mezinárodní konference metalurgie a materiálů /18./, Hradec nad Moravicí (CZ), 2009-05-19 / 2009-05-21
Rok: 2009
Jazyk: eng
Abstrakt: The effect of pre-annealing at 800 °C in argon atmosphere on high temperature corrosion at 1050 °C in air was studied on two high purity nickel grades and compared to a commercial purity nickel. Moreover, the influence of fabrication was analyzed in the case of cast and cold-rolled Puratronic® nickel samples. The mutual grain orientation was measured by means of electron backscatter diffraction and grain boundaries were characterized in terms of the coincidence site lattice model. The scanning electron microscope characterization of cross sections of all the oxidized samples has been performed and compared with the literature. The influence of purity and fabrication on the high temperature oxygen ingress in nickel was discussed in terms of grain boundary character distribution.
Klíčová slova: corrosion; grain boundary; nickel
Číslo projektu: CEZ:AV0Z20410507 (CEP)
Zdrojový dokument: METAL 2009. Conference Proceedings, ISBN 978-80-87294-10-9

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0193516

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-42406


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference