Název: Corrosion of chosen Ni-based material exposed to LiF-NaF molten salts
Autoři: Král, Lubomír ; Čermák, Jiří ; Matal, O. ; Šimo, T. ; Nesvadba, L.
Typ dokumentu: Příspěvky z konference
Konference/Akce: Metal 2010. International Conference on Metallurgy and Materials /19./, Rožnov pod Radhoštěm (CZ), 2010-05-18 / 2010-05-20
Rok: 2010
Jazyk: eng
Abstrakt: This work is devoted to study of changes of structure and chemical composition in the surface layer of chosen candidate alloy Ni – 6 W – 9 Mo – 1.7 Ti – 7 Cr (in wt. %) for components of a LS-VHTR. The material was studied after its exposure to molten mixture 60 mol. % LiF + 40 mol. % NaF at temperature 993 and 1013K. The exposition was carried out in a quasidynamic regime, which simulates coolant (the mixture of salts) natural circulation conditions in components. The structure of the alloy was studied by SEM. Severe corrosion damage was observed in the surface layer, which thickness was about 300 μm.
Klíčová slova: corrosion; molten salts; nickel alloys
Číslo projektu: CEZ:AV0Z20410507 (CEP), 2A-1TP1/067 (CEP)
Poskytovatel projektu: GA MPO
Zdrojový dokument: Metal 2010. 19th International conference on metallurgy and materials - Conference Proceedings, ISBN 978-80-87294-17-8

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0193422

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-42399


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference