An Influence of thermal treatment on the mechanical properties of FeNiB amorphous alloy
Překlad názvu:
Vliv tepelného zpracování na mechanické vlastnosti slitiny FeNiB
Autoři:
Zábranský, Karel ; Jirásková, Yvonna Typ dokumentu: Příspěvky z konference Konference/Akce: Juniormat '05, Brno (CZ), 2005-09-20 / 2005-09-21
Rok:
2005
Jazyk:
eng
Abstrakt: [eng][cze] An influence of thermal treatment in the temperature range 150 - 350 °C on the structural and mechanical properties of an amorphous FeNiB alloy is investigated. The high tensile strength of 2200 MPa in the as-prepared amorphous state slightly decreases with increasing annealing temperature up to approximately 200 °C in opposite to microhardness where an increase is observed. Above 200 °C a pronounced deterioration of both characteristics is observed which reflects the embrittlement of amorphous structure without any indication of crystallization.Byl studován vliv tepelného zpracování v rozsahu 150 - 350 °C na strukturní a mechanické vlastnosti amorfní slitiny na bázi FeNiB. Byla zjištěna vysoká mez pevnosti 2200 Mpa v původním stavu, která se vzrůstající teplotou přibližně do 200 °C klesala, oproti stoupajícím hodnotám mikrotvrdosti. Nad 200°C se obě charakteristiky významně zhoršují, což odráží výrazné zkřehnutí amorfní struktury. Nebyly pozorovány žádné známky krystalizace.
Klíčová slova:
amorphous alloy; microhardness; Mössbauer spectroscopy; tensile test Číslo projektu: CEZ:AV0Z20410507 (CEP) Zdrojový dokument: Juniormat 05, ISBN 80-214-2984-4
Instituce: Ústav fyziky materiálů AV ČR
(web)
Informace o dostupnosti dokumentu:
Dokument je dostupný v příslušném ústavu Akademie věd ČR. Původní záznam: http://hdl.handle.net/11104/0157516