Název: High cycle fatigue life of Ti6Al4V alloy produced by direct metal laser sintering
Autoři: Konečná, R. ; Nicoletto, G. ; Bača, A. ; Kunz, Ludvík
Typ dokumentu: Příspěvky z konference
Konference/Akce: MSMF8. International Conference on Materials Structure and Micromechanics of Fracture /8./, Brno (CZ), 20160627
Rok: 2017
Jazyk: eng
Abstrakt: High cycle fatigue life of Ti6Al4V alloy specimens manufactured by Direct Metal Laser Sintering (DMLS) was experimentally determined. The DMLS fabrication process was characterized by a 400 W laser power and 50 micrometer layer melted thickness. Post-fabrication heat treatment consisted in stress relieving for 3 h at 720 °C in vacuum with subsequent cooling in argon atmosphere. Fatigue testing of specimens oriented in three different directions with respect to the material build direction was performed with the aim to examine the influence of the layered microstructure on the fatigue behavior. Results of measurement of surface roughness, metallographic examinations of the layered material and fractographic investigation of the fatigue fracture surfaces were employed in the discussion of fatigue crack initiation in DMLS fabricated Ti6Al4V alloy.
Klíčová slova: Additive Manufacturing; Fatigue Life; Laser Powder Melting; Titanium Alloy
Zdrojový dokument: Solid State Phenomena, ISBN 978-30-383-5626-4, ISSN 1012-0394
Poznámka: Související webová stránka: https://www.scientific.net/SSP.258.522

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0277072

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-373312


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference