Název: Heterodiffusion of 65Zn in binary Mg - x Al alloys and in a commercial alloy AZ91
Překlad názvu: Heterodifúze 65Zn v binárních slitinách Mg - x Al av komerční slitině AZ91
Autoři: Čermák, Jiří ; Stloukal, Ivo
Typ dokumentu: Příspěvky z konference
Konference/Akce: METAL 2006 - Mezinárodní konference metalurgie a materiálů /15./, Hradec nad Moravicí (CZ), 2006-05-23 / 2006-05-25
Rok: 2006
Jazyk: eng
Abstrakt: [eng] [cze]
Bulk diffusion coefficient of Zn, D, in Mg – x Al model alloys (x = 0, 1.8, 3.9 and 9 at. %), in commercial alloy AZ91 and in intermetallic compound Mg17Al12 intermetallic was measured by residual activity and serial sectioning methods. Composition dependence of D was obtained, that shows a slight increase of D with increasing Al concentration. Measurements were done at several diffusion temperatures, which enabled to evaluate the pre-exponential factor and the activation enthalpy of Zn diffusion. Koeficient objemové difúze Zn, D, v modelových slitinách Mg – x Al (x = 0, 1.8, 3.9 and 9 at. %), v komercní slitine AZ91 a v intermetalické sloucenine Mg17Al12 byl meren metodou zbytkové aktivity a metodou odebírání vrstev. Namerený koeficient D vykazuje mírný nárust s rostoucí koncentrací Al. Merení byla provedena pri nekolika difúzních teplotách, co umožnuje stanovit predexponenciální faktor a aktivacní entalpii difúze Zn.
Klíčová slova: diffusion; magnesium alloy; zinc
Číslo projektu: CEZ:AV0Z20410507 (CEP), GA106/03/1355 (CEP), GA106/05/2115 (CEP)
Poskytovatel projektu: GA ČR, GA ČR
Zdrojový dokument: METAL 2006, ISBN 80-86840-18-2

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0133067

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-35352


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference