Název: An influence of thermal treatment on mechanical properties of FeNiB amorphous alloys
Překlad názvu: Vliv tepelného namáhání na mechanické vlastnosti FeNiB amorfní slitiny
Autoři: Zábranský, Karel ; Jirásková, Yvonna
Typ dokumentu: Příspěvky z konference
Konference/Akce: Juniormat '05, Brno (CZ), 2005-09-20 / 2005-09-21
Rok: 2005
Jazyk: eng
Abstrakt: [eng] [cze]
An influence of thermal treatment in the temperature range of 150 - 350 °C on the structural and mechanical properties of an amorphous FeNiB alloy is investigated. The high tensile strength of 2200 MPa in the as-prepared amorphous state slightly decreases with increasing temperature of annealing up to approximately 200 °C in opposite to microhardness where an increase is observed. Above 200 °C a pronounced deterioration of both characteristics reflect the embrittlement of amorphous structure without any indications of crystallization. Vliv tepelného namáhání v teplotním intervalu 150 - 350 °C na změny struktury a mechanických vlastností je studován na vzorcích FeNiB s amorfní strukturou. Vysoká pevnost v tahu, 2200 MPa, naměřená u vzorku v původním amorfním stavu mírně klesá s rostoucí teplotou žíhání vzorků do přibližně 200 °C na rozdíl od mikrotvrdosti, u níž je pozorován růst. Nad touto teplotou však dochází k výraznému zhoršení obou vlastností vlivem křehnutí amorfní struktury bez jakýchkoliv známek krystalizace.
Klíčová slova: Amorphous; microhardness; tensile testing
Číslo projektu: CEZ:AV0Z20410507 (CEP)
Zdrojový dokument: JUNIORMAT´05, ISBN 80-214-2984-4

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0115238

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-32712


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference