Název:
Studium magnetismu ve sloučeninách CeTX3
Překlad názvu:
Studium magnetismu ve sloučeninách CeTX3
Autoři:
Moudřík, Jan ; Prokleška, Jan (vedoucí práce) ; Javorský, Pavel (oponent) Typ dokumentu: Bakalářské práce
Rok:
2013
Jazyk:
eng
Abstrakt: [eng][cze] Solid solutions of BaNiSn3 type CeTX3 (T and X denote a transition met- al and Si/Ge, respectively) compounds were studied. Polycrystalline samples of solid solutions CeCoxRh1−xSi3 (x = 0.5, x = 0.8, x = 0.9 and x = 1.0) and CeIr(SixGe1−x)3 (x = 0.1, x = 0.4, x = 0.6 and x = 0.8) were successfully grown. A superconducting transition at 0.7-0.9 K was exhibited by all four compositions of the solution CeCoxRh1−xSi3. Based on measurements of specific heat, we con- clude that the superconductivity is probably caused by impurity phases. We have determined crystallographic, thermodynamic and magnetic properties of the solu- tion CeIr(SixGe1−x)3. Magnetic phase transition temperatures were established, the character of the transitions changed significantly in all four compositions, the temperatures themselves did not. 1Studovali jsme tuhé roztoky CeTX3 sloučenin (T a X značí tranzitivní kovy a Si/Ge) s BaNiSn3 strukturou. Úspěšně jsme připravili polykrystalické vzorky CeCoxRh1−xSi3 (x = 0, 5, x = 0, 8, x = 0, 9 a x = 1, 0) a CeIr(SixGe1−x)3 (x = 0, 1, x = 0, 4, x = 0, 6 a x = 0, 8). Všechny 4 vzorky CeCoxRh1−xSi3 přešly do supravodivého stavu při teplotě 0,7-0,9 K. Na základě výsledků měření te- pelné kapacity jsme došli k závěru, že supravodivost je pravděpodobně způsobena příměsí. Určili jsme krystalografické, termodynamické a magnetické vlastnos- ti tuhého roztoku CeIr(SixGe1−x)3 včetně teploty přechodu do magneticky us- pořádaného stavu. Teplota těchto přechodů se ve vzorcích s různou substitucí příliš neměnila, na rozdíl od charakteru přechodů, který se měnil značně. 1
Klíčová slova:
magnetismus; nízké teploty; substituce; low temperature; magnetism; substitution