Original title: Difúze C a Mn ve svarovém spoji Fe-0,3C/Fe-0,3C-15Mn
Translated title: Diffusion of C and Mn in steel weldment Fe-0,3C/Fe-0,3C-15Mn
Authors: Král, L. ; Million, Bořivoj ; Čermák, Jiří
Document type: Papers
Conference/Event: Metallurgical & Material Conference /14./, Hradec nad Moravicí (CZ), 2005-05-24 / 2005-05-26
Year: 2005
Language: cze
Abstract: [cze] [eng]
Příspěvek obsahuje výsledky měření difúze C a Mn ve svarových spojích ternárních slitin Fe-0,3C/Fe-0,3C-15Mn. Slitiny byly odlity v laboratorní indukční peci v ochranné atmosféře Ar. Ingoty byly vykovány do tvaru tyčí kruhového průřezu o průměru cca 15mm a homogenizačně žíhány. Po tepelném zpracování byly obrobeny na průměr 12mm a rozřezány na tloušťku 4mm. Vzorky byly metalograficky broušeny a svařeny elektrickým šokem. Difúzní páry byly ve vakuu zataveny do křemenných ampulí společně s titanovými třískami. Byly žíhány při teplotách 1100-800°C po dobu 1,5-96h. Měření redistribuce uhlíku a manganu bylo provedeno pomocí úsečkové vlnově disperzní mikroanalýzy na rastrovacím mikroskopu Philips SEM-505 s analyzátorem Microspec WDX-2A ve směru kolmém na svarové rozhraní. Byly stanoveny difúzní koeficienty uhlíku a manganu a objasněny vztahy mezi nimi. In the present paper, the results of measurements of C and Mn diffusion in steel weldments of ternary alloys Fe-0.3C/Fe-0.3C-15Mn are reported. Alloys were cast in induction furnace under protective Ar atmosphere. Ingots were hot-forged to rods of the diameter 15mm and homogenized. After annealing they were machined on diameter 12mm and cut into pieces of 4mm thickness. These cylindrical samples were ground and welded by electrical impulse. Diffusion couples were sealed into evacuated silica ampoules together with Ti-chips. They were annealed at 500-1100 °C for 1.5-96 hours. Measurement of carbon and manganese redistribution was done by means line segment microanalysis in normal direction to welded interface using electron scanning microscope Philips SEM-505WDS equiped with Microspec WDX-2A. Diffusion coefficients of C and Mn were obtained and the relations between them were found.
Keywords: up-hill diffusion - Fe-C-Mn
Project no.: CEZ:AV0Z20410507 (CEP), IBS2041105 (CEP)
Funding provider: GA AV ČR
Host item entry: Metal 2005 /14./

Institution: Institute of Physics of Materials AS ČR (web)
Document availability information: Fulltext is available at the institute of the Academy of Sciences.
Original record: http://hdl.handle.net/11104/0112274

Permalink: http://www.nusl.cz/ntk/nusl-32129


The record appears in these collections:
Research > Institutes ASCR > Institute of Physics of Materials
Conference materials > Papers