Název: Fázové transformace ve slitinách na bázi Mg-Zn
Překlad názvu: Phase transformations in Mg-Zn-based alloys
Autoři: Fischer, Josef ; Stulíková, Ivana (vedoucí práce) ; Kekule, Tomáš (oponent)
Typ dokumentu: Diplomové práce
Rok: 2013
Jazyk: cze
Abstrakt: In this thesis MgZnAlCa and MgZnAl materials were studied. For the study of phase transitions on studied materials the method of measuring the changes of resistivity and hardness was used. The measures were carried out at the temperature of 77 K and at the room temperature. Chosen annealing regimes were 20 K / 20 min and also regime without temperature change - 300 řC. Courses of annealing curves are similar. Material MgZnAlCa shows simpler course of annealing curves than material MgZnAl. With both materials the icosahedral quasicrystalis phase was observed. V této práci byly zkoumány materiály MgZnAlCa a MgZnAl. Pro studium fázových změn ve studovaných materiálech byla použita metoda měření změn rezistivity a tvrdosti. Měření probíhala při teplotě 77 K a při pokojové teplotě. Zvolené žíhací režimy byly 20 K / 20 min a dále režim bez změny teploty - 300 řC. Průběhy žíhacích křivek jsou podobné. Materiál MgZnAlCa vykazuje jednodušší průběh žíhacích křivek než materiál MgZnAl. V obou materiálech byla pozorována icosahedrální kvazikrystalická fáze.

Instituce: Fakulty UK (VŠKP) (web)
Informace o dostupnosti dokumentu: Dostupné v digitálním repozitáři UK.
Původní záznam: http://hdl.handle.net/20.500.11956/51681

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-321002


Záznam je zařazen do těchto sbírek:
Školství > Veřejné vysoké školy > Univerzita Karlova > Fakulty UK (VŠKP)
Vysokoškolské kvalifikační práce > Diplomové práce