Autoři: Ševc, P. ; Janovec, J. ; Výrostková, A. ; Svoboda, Milan ; Grabke, H. J. ; Viefhaus, H. ; Mayer, K. H.
Typ dokumentu: Příspěvky z konference
Konference/Akce: Creep & Fracture of Engineering Materials and Structures /10./, Praha (CZ), 2001-04-08 / 2001-04-11
Rok: 2001
Jazyk: eng
Abstrakt: The interfacial and microstructural studies after tempering and long-term aging (steels 9Cr1MoVNbB and 10Cr1Mo1WVNbN) and relaxation strength tests (steel TAF650) were performed. Transgranular cleavage was found to be prevalent fracture mechanism of samples impact fractured at about -100°C. Portion of intergranular facets on analyzed fracture surfaces was extremely low. Low GB concentration of phosphorus (below 1 at.%) was detected in all experimental states. No boron was observed in the AES spectra of the investigated steels.
Klíčová slova: Cr steels; microstructure; segregation
Číslo projektu: CEZ:AV0Z2041904 (CEP), GA106/97/1035 (CEP), 2/1062/21
Poskytovatel projektu: GA ČR, VEGA
Zdrojový dokument: Creep & Fracture of Engineering Materials and Structures, ISSN 1213-3787

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0074645

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-26494


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference