Ševc, P. ; Janovec, J. ; Výrostková, A. ; Svoboda, Milan ; Grabke, H. J. ; Viefhaus, H. ; Mayer, K. H. Typ dokumentu: Příspěvky z konference Konference/Akce: Creep & Fracture of Engineering Materials and Structures /10./, Praha (CZ), 2001-04-08 / 2001-04-11
Rok:
2001
Jazyk:
eng
Abstrakt: The interfacial and microstructural studies after tempering and long-term aging (steels 9Cr1MoVNbB and 10Cr1Mo1WVNbN) and relaxation strength tests (steel TAF650) were performed. Transgranular cleavage was found to be prevalent fracture mechanism of samples impact fractured at about -100°C. Portion of intergranular facets on analyzed fracture surfaces was extremely low. Low GB concentration of phosphorus (below 1 at.%) was detected in all experimental states. No boron was observed in the AES spectra of the investigated steels.
Klíčová slova:
Cr steels; microstructure; segregation Číslo projektu: CEZ:AV0Z2041904 (CEP), GA106/97/1035 (CEP), 2/1062/21 Poskytovatel projektu: GA ČR, VEGA Zdrojový dokument: Creep & Fracture of Engineering Materials and Structures, ISSN 1213-3787
Instituce: Ústav fyziky materiálů AV ČR
(web)
Informace o dostupnosti dokumentu:
Dokument je dostupný v příslušném ústavu Akademie věd ČR. Původní záznam: http://hdl.handle.net/11104/0074645