Název: Creep Resistance and Microstructural Stability of TAF 650 Steel
Autoři: Svoboda, Milan ; Fejfarová, Ivana ; Kroupa, Aleš ; Sklenička, Václav ; Mayer, K. H.
Typ dokumentu: Příspěvky z konference
Konference/Akce: Creep & Fracture of Engineering Materials and Structures /10./, Praha (CZ), 2001-04-08 / 2001-04-11
Rok: 2001
Jazyk: eng
Abstrakt: The quantification of the particles of M23C6 and Laves phase in TAF 650 steel by means of image analysis and thermodynamic calculation of the amount of equilibrium phases were performed. It is shown that the growth rate of Laves phase is substantially higher than that of M23C6 carbide. The total area occupied by Laves phase precipitates represents 52.1 % of all particles area after creep (5888h, 100 MPa, 650 °C). The equilibrium amount of secondary phases calculated by THERMO-Calc is in good agreement with experimental results.
Klíčová slova: Cr steels; microstructural; secondary phases
Číslo projektu: CEZ:AV0Z2041904 (CEP), GA106/00/0855 (CEP), IBS2041105 (CEP)
Poskytovatel projektu: GA ČR, GA AV ČR
Zdrojový dokument: Creep & Fracture of Engineering Materials and Structures, ISSN 1213-3787

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0074644

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-26493


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference