Název: Lithium Sulphur Batteries
Autoři: Juračka, M.
Typ dokumentu: Příspěvky z konference
Jazyk: eng
Nakladatel: Vysoké učení technické v Brně, Fakulta elektrotechniky a komunikačních technologií
Abstrakt: S+C cathode material was prepared by simple solid-state reaction in ball mill. Content of sulphur was approximately 80 wt. % in final sample. Cyclic voltammetry and galvanostatic charge/discharge techniques were used for characterization of the samples. Initial discharge capacity observed for S+C sample was 600 mAh/gsulfur. Capacity loss for S+C sample after 30th cycles was 66 %. Cycling loss is due to insoluble polysulfide formation. In this paper I present fundamental characteristics of Li-S batteries. This paper presents a principle of Li-S batteries, fundamental measurement and their evaluation. I present the techniques of measurement and preparation of cathode materials.
Klíčová slova: batteries; cell; charge; discharge; Li-S; Lithium; polysulfides; Sulfur
Zdrojový dokument: Proceedings of the 21st Conference STUDENT EEICT 2015, ISBN 978-80-214-5148-3

Instituce: Vysoké učení technické v Brně (web)
Informace o dostupnosti dokumentu: Plný text je dostupný v Digitální knihovně VUT.
Původní záznam: http://hdl.handle.net/11012/43023

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-207214


Záznam je zařazen do těchto sbírek:
Školství > Veřejné vysoké školy > Vysoké učení technické v Brně
Konferenční materiály > Příspěvky z konference