Název: Fatigue life and fracture of cast gamma TiAl intermetallic alloy at room and elevated temperatures
Autoři: Petrenec, Martin ; Šmíd, Miroslav ; Polák, Jaroslav
Typ dokumentu: Příspěvky z konference
Konference/Akce: METAL 2011 /20./, Brno (CZ), 2011-05-18 / 2011-05-20
Rok: 2011
Jazyk: eng
Abstrakt: The low-cycle fatigue properties, surface relief and fracture surfaces of cast TiAl alloys with 2 at.% Nb having nearly lamellar microstructure were studied at room temperature and at 750 degrees C. Cyclic stress-strain curves (CSSC) and fatigue life curves were obtained at both temperatures. The surface relief and the fracture surfaces of fractured specimens were observed using scanning electron microscopy. At room temperature, significant cyclic hardening is observed whereas at 750 degrees C cyclic response was stable. Parameters of the CSSC, the Manson-Coffin law and the Basquin law were determined. Persistent slip markings formed along interlamellar interfaces were predominant locations for fatigue cracks at both temperatures. The cracks initiated at surface or in sub-surface region led to the formation of smooth flat areas on the fracture surface corresponding to the persistent slip bands.
Klíčová slova: cast gamma TiAl alloy; elevated temperature; fracture surfaces; low cycle fatigue; PSMs
Číslo projektu: CEZ:AV0Z20410507 (CEP), GAP107/11/0704 (CEP)
Poskytovatel projektu: GA ČR
Zdrojový dokument: METAL 2011 Conference Proceedings - Papers, ISBN 978-80-87294-24-6

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0243315

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-180557


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference