Název: Low Cycle Fatigue and Analysis of the Cyclic Stress-strain Response in Superalloy Inconel 738LC
Autoři: Tobiáš, Jiří ; Chlupová, Alice ; Petrenec, Martin ; Polák, Jaroslav
Typ dokumentu: Příspěvky z konference
Konference/Akce: Engineering Mechanics 2012 /18./, Svratka (CZ), 2012-05-14 / 2012-05-17
Rok: 2012
Jazyk: eng
Abstrakt: The paper describes the results of fatigue behavior study on cast polycrystalline nickel based superalloy tested at 23 and 800 °C. Cylindrical specimens of Inconel 738LC were cyclically strained under total strain control to fracture and multiple step tests were performed to study the effect of temperature on the internal and effective cyclic stress components. Fatigue life curves were approximated by the Manson- Coffin and Basquin laws. The resulting curves were shifted to lower fatigue lives with increasing temperature. The evolution of the effective and internal stress components and effective elastic modules were derived from the hysteresis loops which were analyzed according to the statistical theory of hysteresis loop. Cyclic stress-strain response at both temperatures and the changes of internal and effective stress components were discussed in relation to microstructural parameters of the superalloy.
Klíčová slova: cyclic stress-strain curve; fatigue life curve; hardening/softening curves; Inconel 738LC; low cycle fatigue
Číslo projektu: GAP204/11/1453 (CEP)
Poskytovatel projektu: GA ČR
Zdrojový dokument: Proceedings of Engineering Mechanics 2012, ISBN 978-80-86246-40-6
Poznámka: Související webová stránka: http://www.engmech.cz/2012/proceedings/

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0216718

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-135515


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference