Název: Embrittlement of ferritic 14%Cr ODS steel in air and in Pb/Pb-Bi coolants at elevated temperatures
Autoři: Hadraba, Hynek ; Dlouhý, Ivo ; Hojná, A. ; Di Gabriele, F.
Typ dokumentu: Příspěvky z konference
Konference/Akce: New Methods of Damage and Failure Analysis of Structural Parts, Ostrava (CZ), 2012-09-10 / 2012-09-14
Rok: 2012
Jazyk: eng
Abstrakt: The work was focused to describing influence of long-time high-temperature exposition of the ferritic 14%Cr ODS steel to the liquid Pb and Pb-Bi metals environments. The steel was during exposition in the liquid Pb and Pb-Bi at 600°C and 550°C respectively depleted from Cr and Ti formed with Pb and Bi the surface oxide scale. In addition the isothermal ageing of the steel at 650°C caused precipitates coarsening and porosity development by dislocation annealing in the bulk of the steel. Tensile and impact bend tests reveals outstanding embrittlement of the isothermally aged ODS steel and the steel after exposition to the liquid Pb and Pb-Bi compared with the steel in as-received state.
Klíčová slova: carbide coarsening; impact behaviour; KLST; oxide dispersion strengthened
Číslo projektu: GAP108/10/0466 (CEP)
Poskytovatel projektu: GA ČR
Zdrojový dokument: New Methods of Damage and Failure Analysis of Structural Parts, ISBN 978-80-248-2802-2

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0215269

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-135476


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference