| Hlavní stránka > Konferenční materiály > Příspěvky z konference > Influence of Heat Treatment on Microstructure and Transformation Characteristics of NiTi Shape Memory Wires |
Název:
Influence of Heat Treatment on Microstructure and Transformation Characteristics of NiTi Shape Memory Wires
Autoři: Zálešák, Jakub ; Kuběnová, Monika ; Čermák, Jiří ; Svoboda, Milan ; Dlouhý, Antonín
Typ dokumentu: Příspěvky z konference
Konference/Akce: METAL 2011 /20./, Brno (CZ), 2011-05-18 / 2011-05-20
Rok: 2011
Jazyk: eng
Abstrakt: The present study shows how heat treatments affect microstructure and transformation behaviour of superelastic Ni-rich NiTi shape memory wires. Wire samples were sealed into quartz tubes, filled with hydrogen reduction atmosphere, heated for 10 minutes at temperatures increasing in a range from 500 to 600°C and subsequently quenched into cold water. Characteristic transformation temperatures MS, MF, AS, AF, thermal hysteresis and latent heats were investigated using differential scanning calorimetry (DSC). We observed significant changes in DSC charts which recorded B2 → R and R → B19‘ phase martensitic transformations. Increasing temperature of the heat treatment resulted in a convergence of the two transformation peaks. R-transformation commenced at systematically lower temperatures and the beginning of the B19‘ transformation was shifted to higher temperatures with increasing temperature of the heat treatment. In parallel, latent heat of the overall B2 → B19‘ transformation clearly increases. We rationalize these significant changes in the transformation behaviour on the basis of the microstructural development during the heat treatment which is characterized by means of SEM, TEM and EBSD techniques.
Klíčová slova: Ni-rich NiTi shape memory alloys; phase transformation temperatures; Superelastic wires
Číslo projektu: CEZ:AV0Z20410507 (CEP), GA106/09/1913 (CEP)
Poskytovatel projektu: GA ČR
Zdrojový dokument: METAL 2011 Conference Proceedings, ISBN 978-80-87294-22-2
Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0006936
Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-110451
Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference
Autoři: Zálešák, Jakub ; Kuběnová, Monika ; Čermák, Jiří ; Svoboda, Milan ; Dlouhý, Antonín
Typ dokumentu: Příspěvky z konference
Konference/Akce: METAL 2011 /20./, Brno (CZ), 2011-05-18 / 2011-05-20
Rok: 2011
Jazyk: eng
Abstrakt: The present study shows how heat treatments affect microstructure and transformation behaviour of superelastic Ni-rich NiTi shape memory wires. Wire samples were sealed into quartz tubes, filled with hydrogen reduction atmosphere, heated for 10 minutes at temperatures increasing in a range from 500 to 600°C and subsequently quenched into cold water. Characteristic transformation temperatures MS, MF, AS, AF, thermal hysteresis and latent heats were investigated using differential scanning calorimetry (DSC). We observed significant changes in DSC charts which recorded B2 → R and R → B19‘ phase martensitic transformations. Increasing temperature of the heat treatment resulted in a convergence of the two transformation peaks. R-transformation commenced at systematically lower temperatures and the beginning of the B19‘ transformation was shifted to higher temperatures with increasing temperature of the heat treatment. In parallel, latent heat of the overall B2 → B19‘ transformation clearly increases. We rationalize these significant changes in the transformation behaviour on the basis of the microstructural development during the heat treatment which is characterized by means of SEM, TEM and EBSD techniques.
Klíčová slova: Ni-rich NiTi shape memory alloys; phase transformation temperatures; Superelastic wires
Číslo projektu: CEZ:AV0Z20410507 (CEP), GA106/09/1913 (CEP)
Poskytovatel projektu: GA ČR
Zdrojový dokument: METAL 2011 Conference Proceedings, ISBN 978-80-87294-22-2
Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0006936
Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-110451
Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference
Záznam vytvořen dne 2012-04-03, naposledy upraven 2024-01-26.