Processing of compact polycrystalline YAG ceramics
Kaplan, Lukáš ; Pouchlý, Václav (referee) ; Kachlík, Martin (advisor)
In the literary part of this master thesis a research on various methods of preparation of dense polycrystalline YAG ceramics and the effects of sintering on the densification and other desired properties of such prepared YAG ceramics was carried out, the transparency after addition of dopant elements was also discussed. In the experimental part of the thesis, samples of dense polycrystalline YAG ceramics were prepared by SSR method and the effect of sintering on the densification and porosity of the YAG ceramic samples was studied. Relative density, porosity, phase purity and transparency were measured on the sintered samples. These measurements were compared with the results of the works reported in the literature section.
|
|
|
Machining of ceramic bodies using CAD-CAM
Kaplan, Lukáš ; Částková, Klára (referee) ; Kaštyl, Jaroslav (advisor)
The literature part of bachelor's thesis deals with ceramic materials based on Al2O3 and ZrO2, methods of sample preparation for consequent machining, different methods of machining, especially the technology of CNC machining in non-sintered and sintered state with their comparison. The thesis presents possible examples of the use of ceramic parts. The experimental part of the thesis deals with the machining of ceramic based on ZrO2 using different types of ceramic powders, methods of preparation and the choice of the sintered temperature in relation to its properties. The best results were achieved with SZ-3Y ceramic material sintered at 1550 °C for 2 hours, strength values were 1203 MPa, roughness of surface Ra was 126 nm a grain size was 382 nm.
|
|
| |
|
|
Processing of compact polycrystalline YAG ceramics
Kaplan, Lukáš ; Pouchlý, Václav (referee) ; Kachlík, Martin (advisor)
In the literary part of this master thesis a research on various methods of preparation of dense polycrystalline YAG ceramics and the effects of sintering on the densification and other desired properties of such prepared YAG ceramics was carried out, the transparency after addition of dopant elements was also discussed. In the experimental part of the thesis, samples of dense polycrystalline YAG ceramics were prepared by SSR method and the effect of sintering on the densification and porosity of the YAG ceramic samples was studied. Relative density, porosity, phase purity and transparency were measured on the sintered samples. These measurements were compared with the results of the works reported in the literature section.
|
|
|
Machining of ceramic bodies using CAD-CAM
Kaplan, Lukáš ; Částková, Klára (referee) ; Kaštyl, Jaroslav (advisor)
The literature part of bachelor's thesis deals with ceramic materials based on Al2O3 and ZrO2, methods of sample preparation for consequent machining, different methods of machining, especially the technology of CNC machining in non-sintered and sintered state with their comparison. The thesis presents possible examples of the use of ceramic parts. The experimental part of the thesis deals with the machining of ceramic based on ZrO2 using different types of ceramic powders, methods of preparation and the choice of the sintered temperature in relation to its properties. The best results were achieved with SZ-3Y ceramic material sintered at 1550 °C for 2 hours, strength values were 1203 MPa, roughness of surface Ra was 126 nm a grain size was 382 nm.
|
|
| |