Název:
High strain-rate compressive testing of filling materials for inter-penetrating phase composites
Autoři: Doktor, T. ; Fíla, T. ; Zlámal, Petr ; Kytýř, Daniel ; Jiroušek, O.
Typ dokumentu: Příspěvky z konference
Konference/Akce: Youth Symposium on Experimental Solid Mechanics /17./, Telč (CZ), 20190606
Rok: 2019
Jazyk: eng
Abstrakt: In this study behavior of the selected types of filling material for the inter-penetrating phase composites was tested in compressive loading mode at low and high strain-rates. Three types of the filling material were tested, (i) ordnance gelatin, (ii) low expansion polyurethane foam, and (iii) polyurethane putty. To evaluate their impact energy absorption bulk samples of the selected materials were tested in compression loading mode at strain-rates 1000 s−1 to 4000 s−1. The high strain-rate compressive loading was provided by Split Hopkinson Pressure Bar (SHPB) which was equipped with PMMA bars to enable testing of cellular materials with low mechanical impedance. Based on the comparative measurement response to compression at both low and high strain-rates was analysed. The results show a significant strain-rate sensitivity of the ordnance gelatin and of the polyurethane putty, while strain-rate effect in the polyurethane foam was not observed.
Klíčová slova: impact protection filling materials; interpenetration phase composite; SHPB; strain-rate sensitivity
Číslo projektu: EF16_019/0000766
Poskytovatel projektu: GA MŠk
Zdrojový dokument: Acta Polytechnica CTU Proceedings, ISBN 978-80-01-06670-6
Poznámka: Související webová stránka: https://ojs.cvut.cz/ojs/index.php/APP/article/view/6015
Instituce: Ústav teoretické a aplikované mechaniky AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0300560
Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-408939
Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav teoretické a aplikované mechaniky
Konferenční materiály > Příspěvky z konference
Autoři: Doktor, T. ; Fíla, T. ; Zlámal, Petr ; Kytýř, Daniel ; Jiroušek, O.
Typ dokumentu: Příspěvky z konference
Konference/Akce: Youth Symposium on Experimental Solid Mechanics /17./, Telč (CZ), 20190606
Rok: 2019
Jazyk: eng
Abstrakt: In this study behavior of the selected types of filling material for the inter-penetrating phase composites was tested in compressive loading mode at low and high strain-rates. Three types of the filling material were tested, (i) ordnance gelatin, (ii) low expansion polyurethane foam, and (iii) polyurethane putty. To evaluate their impact energy absorption bulk samples of the selected materials were tested in compression loading mode at strain-rates 1000 s−1 to 4000 s−1. The high strain-rate compressive loading was provided by Split Hopkinson Pressure Bar (SHPB) which was equipped with PMMA bars to enable testing of cellular materials with low mechanical impedance. Based on the comparative measurement response to compression at both low and high strain-rates was analysed. The results show a significant strain-rate sensitivity of the ordnance gelatin and of the polyurethane putty, while strain-rate effect in the polyurethane foam was not observed.
Klíčová slova: impact protection filling materials; interpenetration phase composite; SHPB; strain-rate sensitivity
Číslo projektu: EF16_019/0000766
Poskytovatel projektu: GA MŠk
Zdrojový dokument: Acta Polytechnica CTU Proceedings, ISBN 978-80-01-06670-6
Poznámka: Související webová stránka: https://ojs.cvut.cz/ojs/index.php/APP/article/view/6015
Instituce: Ústav teoretické a aplikované mechaniky AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0300560
Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-408939
Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav teoretické a aplikované mechaniky
Konferenční materiály > Příspěvky z konference
Záznam vytvořen dne 2020-01-13, naposledy upraven 2021-11-24.