Microstructural changes in creep of TAF 650 steel at 650řC
Autoři:
Svoboda, Milan ; Dlouhý, Antonín ; Fejfarová, Ivana ; Sklenička, Václav ; Mayer, K. H. Typ dokumentu: Příspěvky z konference Konference/Akce: METAL 2000 - Mezinárodní metalurgická konference /9./, Ostrava (CZ), 2000-05-16 / 2000-05-18
Rok:
2000
Jazyk:
eng
Abstrakt: The microstructure of high chromium martensitic steel TAF 650 was quantified by transmission electron microscopy and image analysis in virgin condition and after creep at 650řC for 4379 and 5888 h where marked decrease in time to fracture occurred. It is concluded that preferential recovery of regions without subgrains in virgin conditions and pronounced coarsening of Laves phase Fe2W, are responsible for an observed decrease in creep life. Číslo projektu: IBS2041001 (CEP), OC 522.40 Poskytovatel projektu: GA AV ČR, GA MŠk Zdrojový dokument: METAL 2000 - 9. mezinárodní metalurgická konference
Instituce: Ústav fyziky materiálů AV ČR
(web)
Informace o dostupnosti dokumentu:
Dokument je dostupný v příslušném ústavu Akademie věd ČR. Původní záznam: http://hdl.handle.net/11104/0074366