Název: Microstructure and Properties of Spark Plasma Sintered Al-Zn-Mg-Cu Alloy.
Autoři: Zyka, J. ; Málek, J. ; Pala, Zdeněk ; Andršová, I. ; Veselý, J.
Typ dokumentu: Příspěvky z konference
Konference/Akce: METAL 2015 - International Conference on Metallurgy and Materials /24./, Brno (CZ), 20160603
Rok: 2015
Jazyk: eng
Abstrakt: High entropy alloys are a new material class with promising structural and mechanical properties in wide range of applications. In principle they consist of five or more elements in equimolar concentrations resulting basically in single phase microstructure. TaNbHfZrTi alloy was developed by Senkov for high temperature applications.\nSince all of these elements are biocompatible the TaNbHfZrTi alloy can be investigated as a prospective bio implant material. The alloy was prepared by vacuum arc melting, no annealing treatment was applied. Tensile test and hardness test at room temperature were performed with very good results: yield strength 1155 MPa, rupture strength 1212 MPa, Vickers hardness 359 HV30. Microstructure and fracture morphology was also investigated.
Klíčová slova: High Entropy Alloys; Mechanical Properties; Microstructure; Tensile Test
Zdrojový dokument: METAL 2015: 24th International Conference on Metallurgy and Materials, Conference Proceedings, ISBN 978-80-87294-62-8

Instituce: Ústav fyziky plazmatu AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0270354

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-263591


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky plazmatu
Konferenční materiály > Příspěvky z konference