Název: Fatigue crack growth in 316L under uniaxial and torsional loading
Autoři: Karol, Michal ; Chlupová, Alice ; Mazánová, Veronika ; Kruml, Tomáš
Typ dokumentu: Příspěvky z konference
Konference/Akce: METAL 2016 - Anniversary International Conference on Metallurgy and Materials /25./, Brno (CZ), 20160525
Rok: 2016
Jazyk: eng
Abstrakt: A study of fatigue crack initiation and growth in 316L austenitic stainless steel is reported. Fatigue experiments were performed at room temperature on full cylindrical specimens cycled axially (tension-compression) and on hollow cylindrical specimens tested in reversed torsion. Microstructure and damage evolution (crack initiation and growth) on the surface of mechanically and electrolytically polished specimens were observed using light and electron microscopy. An analysis of the orientation of microcracks and macrocracks which led to failure was made. Axially loaded specimens exhibited presence of several microcracks which resulted in macrocrack propagating perpendicularly to specimen axis. In the case of torsional loading, orientation of macrocrack propagation was dependent on applied load and presence of notches. High amount of short cracks initiated parallel to specimen axis. Long cracks exhibited a tendency to bifurcate with crack branches oriented at approximately 45° to the specimen axis.
Klíčová slova: 316L austenitic steel; fatigue; surface relief
Číslo projektu: GA15-08826S (CEP), LM2015069 (CEP)
Poskytovatel projektu: GA ČR, GA MŠk
Zdrojový dokument: METAL 2016: 25th International Conference on Metallurgy and Materials, ISBN 978-80-87294-67-3

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0266919

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-262621


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference