Název: HYDROGEN STORAGE IN Mg-In-C ALLOYS: EFFECT OF COMPOSITION AND AGEING
Autoři: Čermák, Jiří ; Král, Lubomír
Typ dokumentu: Příspěvky z konference
Konference/Akce: METAL 2015 - International Conference on Metallurgy and Materials /24./, Brno (CZ), 2015-06-03 / 2015-06-05
Rok: 2015
Jazyk: eng
Abstrakt: Hydrogen storage in two Mg-In-C alloys with different In concentration, c In , was studied in the temperature range from 250°C to 350°C after five-years-ageing at room temperature. The both alloys show acceptable cycling stability, however, the storage capacity of the alloys decreased from about 5 wt. % H2 to about 2,5 and 3.1 wt. % H 2 by higher c In and lower c In , respectively after 5 years. The sorption kinetics degraded much more by high c In than by c In . PCT isotherms, TPS and DSC patterns were measured for both materials. It was found that the hydrides responsible for hydrogen storage in alloy with higher c In are slightly more stable.
Klíčová slova: hydrogen; hydrogen storage; magnesium alloys
Číslo projektu: ED1.1.00/02.0068
Poskytovatel projektu: GA MŠk
Zdrojový dokument: Metal 2015: 24th International Conference on Metallurgy and Materials, ISBN 978-80-87294-58-1

Instituce: Ústav fyziky materiálů AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný v příslušném ústavu Akademie věd ČR.
Původní záznam: http://hdl.handle.net/11104/0250488

Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-200729


Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav fyziky materiálů
Konferenční materiály > Příspěvky z konference