Original title: Stanoveni koeficientu délkové teplotní roztažnosti slinuté PZT keramiky
Translated title: Determination of the coefficient of linear thermal expansion of sintered PZT ceramics
Authors: Šašek, Petr
Document type: Research reports
Year: 2015
Language: cze
Abstract: [cze] [eng]
When a material is subjected to heating, a change of its dimensions may occur. This can be a problem, in case that the individual layers have different expansion properties. The aim of this study was to determine the thermal expansion coefficient of piezoelectric ceramics with thin layer of silver. The temperature range was from -20 to +60 °C and for one sample from -30 to +160 °C. The heating rate was 1 °C/min. Three samples were measured. The comparison of thermal expansion shows, that one of the samples differs from the other two, the latter having similar properties. Působením teploty dochází v materiálech ke změnám velikosti. Toto může být problém v případě, že se jedná o vrstevnatý materiál, kdy jednotlivé vrstvy mají rozdílné vlastnosti. Cílem této studie bylo zjistit součinitel teplotní roztažnosti piezoelektrické keramiky s tenkou stříbrnou vrstvou. Teplotní rozsah byl od -20 do 60 °C, resp. od -30 do 160 °C. Rychlost ohřevu byla 1°C/min. Celkem byly měřeny 3 vzorky. Srovnání tepelné roztažnosti nám ukazuje, že jeden vzorek se liší od dvou vzorků, které mají podobné vlastnosti.
Keywords: dilatation; piezoelectric ceramics; thermal expansion coefficient

Institution: Institute of Theoretical and Applied Mechanics AS ČR (web)
Document availability information: Fulltext is available on demand via the digital repository of the Academy of Sciences.
Original record: http://hdl.handle.net/11104/0250148

Permalink: http://www.nusl.cz/ntk/nusl-200725


The record appears in these collections:
Research > Institutes ASCR > Institute of Theoretical and Applied Mechanics
Reports > Research reports