| Hlavní stránka > Konferenční materiály > Příspěvky z konference > NANOSTRUCTURE CHARACTERIZATION OF IN738LC SUPERALLOY FATIGUED AT HIGH TEMPERATURE |
Název:
NANOSTRUCTURE CHARACTERIZATION OF IN738LC SUPERALLOY FATIGUED AT HIGH TEMPERATURE
Autoři: Petrenec, M. ; Strunz, Pavel ; Gasser, U. ; Heczko, Milan ; Zálešák, J. ; Polák, Jaroslav
Typ dokumentu: Příspěvky z konference
Konference/Akce: 5th International Conference NANOCON, Brno (CZ), 20131016
Rok: 2013
Jazyk: eng
Abstrakt: The nanostructure of Inconel 738LC Ni-superalloy strengthened by trimodal Y precipitates distribution was investigated after Low Cycle Fatigue (LFC) loading at temperature 700°C. Different microscopic techniques as Scanning Electron Microscope (SEM) equipped with STEM detectro, transmission Kikuchi diffraction in the SEM, transmission electron microscope (TEM) in the bright field mode and high resolution transmission electron mciroscopes (HRTEM) in STEM mode were used for the characterization and quantification of superalloy nanostructure. The characteristic morphology of y precipitates was examined by ex-situ and in-situ Small Angle Neutron Scattering (SANS) at high temperatures. All adopted microscopic techniques indicate that the morphology of y precipitates distributed in the y matrix as recived state corresponds to two types, i.e. large cuboid-like precipitates with the size around 670 nm, and the spherical precipitates with the diameter 52nm. After eh LCF tests at temperature 700°C, the ex-situ SANS measurement yielded addititonal scattering intensities coming from another small y precipitetes with estimated size up to 10nm.
Klíčová slova: nano-precipitation; neutron scattering; STEM detector; superalloys; TEM
Číslo projektu: GAP204/11/1453 (CEP), LM2011019 (CEP)
Poskytovatel projektu: GA ČR, GA MŠk
Zdrojový dokument: NANOCON 2013, ISBN 978-80-87294-44-4
Instituce: Ústav jaderné fyziky AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný na externích webových stránkách.
Externí umístění souboru: http://www.nanocon.eu/files/proceedings/14/reports/2001.pdf
Původní záznam: http://hdl.handle.net/11104/0228125
Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-166237
Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav jaderné fyziky
Konferenční materiály > Příspěvky z konference
Autoři: Petrenec, M. ; Strunz, Pavel ; Gasser, U. ; Heczko, Milan ; Zálešák, J. ; Polák, Jaroslav
Typ dokumentu: Příspěvky z konference
Konference/Akce: 5th International Conference NANOCON, Brno (CZ), 20131016
Rok: 2013
Jazyk: eng
Abstrakt: The nanostructure of Inconel 738LC Ni-superalloy strengthened by trimodal Y precipitates distribution was investigated after Low Cycle Fatigue (LFC) loading at temperature 700°C. Different microscopic techniques as Scanning Electron Microscope (SEM) equipped with STEM detectro, transmission Kikuchi diffraction in the SEM, transmission electron microscope (TEM) in the bright field mode and high resolution transmission electron mciroscopes (HRTEM) in STEM mode were used for the characterization and quantification of superalloy nanostructure. The characteristic morphology of y precipitates was examined by ex-situ and in-situ Small Angle Neutron Scattering (SANS) at high temperatures. All adopted microscopic techniques indicate that the morphology of y precipitates distributed in the y matrix as recived state corresponds to two types, i.e. large cuboid-like precipitates with the size around 670 nm, and the spherical precipitates with the diameter 52nm. After eh LCF tests at temperature 700°C, the ex-situ SANS measurement yielded addititonal scattering intensities coming from another small y precipitetes with estimated size up to 10nm.
Klíčová slova: nano-precipitation; neutron scattering; STEM detector; superalloys; TEM
Číslo projektu: GAP204/11/1453 (CEP), LM2011019 (CEP)
Poskytovatel projektu: GA ČR, GA MŠk
Zdrojový dokument: NANOCON 2013, ISBN 978-80-87294-44-4
Instituce: Ústav jaderné fyziky AV ČR (web)
Informace o dostupnosti dokumentu: Dokument je dostupný na externích webových stránkách.
Externí umístění souboru: http://www.nanocon.eu/files/proceedings/14/reports/2001.pdf
Původní záznam: http://hdl.handle.net/11104/0228125
Trvalý odkaz NUŠL: http://www.nusl.cz/ntk/nusl-166237
Záznam je zařazen do těchto sbírek:
Věda a výzkum > AV ČR > Ústav jaderné fyziky
Konferenční materiály > Příspěvky z konference
Záznam vytvořen dne 2013-12-26, naposledy upraven 2021-11-24.