Corrosion resistance of cast duplex stainless steels
Müller, Peter ; Záděra, Antonín (oponent) ; Pernica, Vítězslav (vedoucí práce)
The master’s thesis deals with corrosion resistance of cast duplex steels. In the first part the corrosion mechanisms and their individual types are described, the second part characterizes the types of stainless steels in terms of their properties, use, structural components, and their impact on mechanical and corrosion properties of steels. Individual chapter is dedicated to duplex steels. In the experimental part the resistance of 1.4517 steel against pitting corrosion depending on the alloy contents and the PREN value was investigated. Four specimens graded according to PREN were cast. Supplemented with sample stirrer blade which was affected by corrosion during service they were subjected to corrosion test according to ASTM G48-11 standard in 6% FeCl3 solution. Cast specimens were subjected to tensile test and impact test.
|
|
|
Vliv vneseného tepla na vlastnosti a strukturu svarového spoje duplexní oceli.
Němec, Karel ; Kubíček, Jaroslav (oponent) ; Daněk, Ladislav (vedoucí práce)
Projekt vypracovaný v rámci magisterského studia oboru strojírenská technologie se zabývá zkoumáním vlivu vneseného tepla na vlastnosti a strukturu duplexní oceli jakosti 1.4462. Zkušební vzorky, na kterých byly provedeny nátavy při rychlosti svařování 10, 15, 20, 25, 30 cm.min-1, byly podrobeny zkoušce tahem, metalografické analýze a zkoušce tvrdosti. Výsledky zkoušek prokázaly, že při tloušťce materiálu 2 mm je nejvhodnější rychlost svařování pro nátavy 15 cm.min-1. Při rychlosti svařování 10 cm.min-1 již vznikaly horké trhliny zatímco při rychlosti 20, 25, 30 cm.min-1 nedošlo k průvaru materiálu.
|
|
| |
|
|
Vliv chemického složení oceli na strukturu a vlastnosti korozivzdorných ocelí
Valenta, Pavel ; Čech, Jan (oponent) ; Záděra, Antonín (vedoucí práce)
Tato diplomová práce je zaměřená na vysokolegované austenitické a austeniticko-feritické (duplexní) oceli. Teoretická část práce zahrnuje rozdělení vysokolegovaných ocelí a základní seznámení s touto problematikou. V praktické části byly provedeny zkušební tavby austenitické žáropevné oceli 30CH3N17G2L, korozivzdorné duplexní oceli 1.4462, nízkouhlíkové oceli a vysokouhlíkové oceli. Na odlitcích z austenitické oceli byly provedeny mechanické a technologické zkoušky. Byly hodnoceny vlivy rozdílné licí teploty a tloušťky stěn odlitků na mikro a makro strukturu oceli, tahovou pevnost a nárazovou práci. V rámci technologických zkoušek byly porovnávány technologické vlastnosti zmíněných ocelí.
|
|
|
Corrosion resistance of cast duplex stainless steels
Müller, Peter ; Záděra, Antonín (oponent) ; Pernica, Vítězslav (vedoucí práce)
The master’s thesis deals with corrosion resistance of cast duplex steels. In the first part the corrosion mechanisms and their individual types are described, the second part characterizes the types of stainless steels in terms of their properties, use, structural components, and their impact on mechanical and corrosion properties of steels. Individual chapter is dedicated to duplex steels. In the experimental part the resistance of 1.4517 steel against pitting corrosion depending on the alloy contents and the PREN value was investigated. Four specimens graded according to PREN were cast. Supplemented with sample stirrer blade which was affected by corrosion during service they were subjected to corrosion test according to ASTM G48-11 standard in 6% FeCl3 solution. Cast specimens were subjected to tensile test and impact test.
|
|
| |
|
|
Vliv chemického složení oceli na strukturu a vlastnosti korozivzdorných ocelí
Valenta, Pavel ; Čech, Jan (oponent) ; Záděra, Antonín (vedoucí práce)
Tato diplomová práce je zaměřená na vysokolegované austenitické a austeniticko-feritické (duplexní) oceli. Teoretická část práce zahrnuje rozdělení vysokolegovaných ocelí a základní seznámení s touto problematikou. V praktické části byly provedeny zkušební tavby austenitické žáropevné oceli 30CH3N17G2L, korozivzdorné duplexní oceli 1.4462, nízkouhlíkové oceli a vysokouhlíkové oceli. Na odlitcích z austenitické oceli byly provedeny mechanické a technologické zkoušky. Byly hodnoceny vlivy rozdílné licí teploty a tloušťky stěn odlitků na mikro a makro strukturu oceli, tahovou pevnost a nárazovou práci. V rámci technologických zkoušek byly porovnávány technologické vlastnosti zmíněných ocelí.
|
|
|
Vliv vneseného tepla na vlastnosti a strukturu svarového spoje duplexní oceli.
Němec, Karel ; Kubíček, Jaroslav (oponent) ; Daněk, Ladislav (vedoucí práce)
Projekt vypracovaný v rámci magisterského studia oboru strojírenská technologie se zabývá zkoumáním vlivu vneseného tepla na vlastnosti a strukturu duplexní oceli jakosti 1.4462. Zkušební vzorky, na kterých byly provedeny nátavy při rychlosti svařování 10, 15, 20, 25, 30 cm.min-1, byly podrobeny zkoušce tahem, metalografické analýze a zkoušce tvrdosti. Výsledky zkoušek prokázaly, že při tloušťce materiálu 2 mm je nejvhodnější rychlost svařování pro nátavy 15 cm.min-1. Při rychlosti svařování 10 cm.min-1 již vznikaly horké trhliny zatímco při rychlosti 20, 25, 30 cm.min-1 nedošlo k průvaru materiálu.
|