Using of X-ray for distribution analysis of electrodes for secondary cell application
Macháč, Milan ; Bača, Petr (referee) ; Chladil, Ladislav (advisor)
This diploma thesis is focused on in-situ analysis of the composition of the negative electrodes of second secondary cells with using X-ray radiation. The first part is dedicated to the theory of lead accumulators, including charging, discharging, battery components and individual degradation mechanisms. The main part of the thesis includes the preparation of electrochemical in situ XRD cells and following measurement of the growth of lead sulphate crystals on the OCV potential. Furthermore, the lead cell was subjected to the measurement of the cyclic voltammetry around the working point of the negative electrodes. From these measurements was evident gradual increase of the lead sulfate crystals. The analysis was supplemented with electron microscopy images. In addition, were evaluated the in-situ particle analysis of the LTO Sigma sample.
|
|
|
Design and evaluation of process equipment damaged by degradation mechanisms
Cablková, Zuzana ; Naď, Martin (referee) ; Lošák, Pavel (advisor)
This bachelor thesis is aimed at the evaluation of selected degradation mechanisms which occurs in process equipment. The assessment is undoubtedly important in terms of safety and prediction of residual life. This issue is demonstrated by two mechanisms described in this thesis. A phenomenon called creep is the first of these mechanisms and appears in environments with elevated temperature. The theoretical part of the thesis covers the basic principles of the creep mechanism and its effect on the material. A marginal but not negligible problem is the occurrence of this damage in welded joints. Many standards deal with the prediction and assessment of creep. Part of this thesis is the mapping and to some extent a comparison of several selected procedures. The second degradation mechanism is related to the presence of aggressive compounds such as sulfide. This can lead to hydrogen embrittlement, blisters, and many other damages. As with creep, an overview of standards devoted to the design, evaluation, or maintenance of equipment used in this way is created for these mechanisms. The content of the practical part of this thesis is the calculation of the evaluation of such a device by using the procedures of the API 579-1 standard.
|
|
|
Life management of power oil transformer
Čechová, Karolína ; Froehling, Kenneth (referee) ; Sedláček, Pavel (advisor)
Pro pochopení významu procesu řízení životnosti výkonových olejových transformátorů, je nutné si nejdříve uvědomit jejich roli v elektrizační soustavě. Používají se především ke zvýšení a snížení napěťových úrovní v přenosové a distribuční soustavě dle aktuálních potřeb. Nespolehlivost výkonových olejových transformátorů může způsobit narušení stability dodávky elektrické energie, což představuje značné finanční a technické ztráty pro společnosti, které spravují tento typ zařízení. Z tohoto důvodu jsem se rozhodla napsat práci, která poskytuje přehled o procesu řízení životnosti, popsáním jeho ekonomických přínosů spolu s technickými diagnostikami, které napomáhají ke zjištění vznikajících poruch během provozu výkonových olejových transformátorů. Hlavním záměrem této práce je popsat a dokázat důležitost procesu řízení životnosti a využití diagnostických metod ke sledování parametrů transformátoru, které slouží jako prostředek ke zjištění možných poruch. Praktická část je zaměřena na navržení vhodných diagnostickým metod pro měření zvolených parametrů vybraného výkonového olejového transformátoru. Poté je provedena analýza zvolených parametrů a na základě jejích výsledků, je určen celkový stav vybraného výkonového olejového transformátoru.
|
|
|
Monitoring of Electrode Changes of Negative Electrode for Lead-Acid Batteries by Operando Confocal Microscopy
Hálová, Hana ; Vanýsek, Petr (referee) ; Chladil, Ladislav (advisor)
The thesis is focused on the laser microscopy observation of the negative electrode for lead-acid batteries during their cycling. The surface changes are evaluated during both deep cycling and PSoC (Partial State of Charge) cycling. The mode leads to gradual degradation of the negative electrode – mostly because of irreversible sulfation. The speed of the sulfation can be influnced by additives of the negative active mass added already during production process. The active mass was firstly examined by electron microscope and X-ray diffractometer. The crystal growth during cycling was observed using confocal microscope Olympus Lext OLS4100.
|
|
|
Degradation mechanisms of lead-acid batteries
Pavlů, Michal ; Abraham, Pavel (referee) ; Bača, Petr (advisor)
This work deals with problems of degradation mechanisms of lead-acid batteries. For a better understanding of the diverse effects that cause the degradation are analyzed and the physical explanation of each of the degradation mechanisms. The paper describes the measuring method by which they examined the different manifestations of degradation mechanisms. At the conclusion of works are carried out measurements in which it is possible to trace the manifestations of the various degradation mechanisms in lead battery taking place mainly on the active surface electrodes.
|
|
|
Design and evaluation of process equipment damaged by degradation mechanisms
Cablková, Zuzana ; Naď, Martin (referee) ; Lošák, Pavel (advisor)
This bachelor thesis is aimed at the evaluation of selected degradation mechanisms which occurs in process equipment. The assessment is undoubtedly important in terms of safety and prediction of residual life. This issue is demonstrated by two mechanisms described in this thesis. A phenomenon called creep is the first of these mechanisms and appears in environments with elevated temperature. The theoretical part of the thesis covers the basic principles of the creep mechanism and its effect on the material. A marginal but not negligible problem is the occurrence of this damage in welded joints. Many standards deal with the prediction and assessment of creep. Part of this thesis is the mapping and to some extent a comparison of several selected procedures. The second degradation mechanism is related to the presence of aggressive compounds such as sulfide. This can lead to hydrogen embrittlement, blisters, and many other damages. As with creep, an overview of standards devoted to the design, evaluation, or maintenance of equipment used in this way is created for these mechanisms. The content of the practical part of this thesis is the calculation of the evaluation of such a device by using the procedures of the API 579-1 standard.
|
|
|
Monitoring of Electrode Changes of Negative Electrode for Lead-Acid Batteries by Operando Confocal Microscopy
Hálová, Hana ; Vanýsek, Petr (referee) ; Chladil, Ladislav (advisor)
The thesis is focused on the laser microscopy observation of the negative electrode for lead-acid batteries during their cycling. The surface changes are evaluated during both deep cycling and PSoC (Partial State of Charge) cycling. The mode leads to gradual degradation of the negative electrode – mostly because of irreversible sulfation. The speed of the sulfation can be influnced by additives of the negative active mass added already during production process. The active mass was firstly examined by electron microscope and X-ray diffractometer. The crystal growth during cycling was observed using confocal microscope Olympus Lext OLS4100.
|
|
|
Life management of power oil transformer
Čechová, Karolína ; Froehling, Kenneth (referee) ; Sedláček, Pavel (advisor)
Pro pochopení významu procesu řízení životnosti výkonových olejových transformátorů, je nutné si nejdříve uvědomit jejich roli v elektrizační soustavě. Používají se především ke zvýšení a snížení napěťových úrovní v přenosové a distribuční soustavě dle aktuálních potřeb. Nespolehlivost výkonových olejových transformátorů může způsobit narušení stability dodávky elektrické energie, což představuje značné finanční a technické ztráty pro společnosti, které spravují tento typ zařízení. Z tohoto důvodu jsem se rozhodla napsat práci, která poskytuje přehled o procesu řízení životnosti, popsáním jeho ekonomických přínosů spolu s technickými diagnostikami, které napomáhají ke zjištění vznikajících poruch během provozu výkonových olejových transformátorů. Hlavním záměrem této práce je popsat a dokázat důležitost procesu řízení životnosti a využití diagnostických metod ke sledování parametrů transformátoru, které slouží jako prostředek ke zjištění možných poruch. Praktická část je zaměřena na navržení vhodných diagnostickým metod pro měření zvolených parametrů vybraného výkonového olejového transformátoru. Poté je provedena analýza zvolených parametrů a na základě jejích výsledků, je určen celkový stav vybraného výkonového olejového transformátoru.
|
|
|
Using of X-ray for distribution analysis of electrodes for secondary cell application
Macháč, Milan ; Bača, Petr (referee) ; Chladil, Ladislav (advisor)
This diploma thesis is focused on in-situ analysis of the composition of the negative electrodes of second secondary cells with using X-ray radiation. The first part is dedicated to the theory of lead accumulators, including charging, discharging, battery components and individual degradation mechanisms. The main part of the thesis includes the preparation of electrochemical in situ XRD cells and following measurement of the growth of lead sulphate crystals on the OCV potential. Furthermore, the lead cell was subjected to the measurement of the cyclic voltammetry around the working point of the negative electrodes. From these measurements was evident gradual increase of the lead sulfate crystals. The analysis was supplemented with electron microscopy images. In addition, were evaluated the in-situ particle analysis of the LTO Sigma sample.
|
|
|
Degradation mechanisms of lead-acid batteries
Pavlů, Michal ; Abraham, Pavel (referee) ; Bača, Petr (advisor)
This work deals with problems of degradation mechanisms of lead-acid batteries. For a better understanding of the diverse effects that cause the degradation are analyzed and the physical explanation of each of the degradation mechanisms. The paper describes the measuring method by which they examined the different manifestations of degradation mechanisms. At the conclusion of works are carried out measurements in which it is possible to trace the manifestations of the various degradation mechanisms in lead battery taking place mainly on the active surface electrodes.
|